Effect of Li+ on Luminescence Properties and Thermal Stability of Glass Ceramics Containing SrMoO4

Zhiqian Lv,Shuting Zhao,Rong Wang,Yihan Cheng,Dandan Li,Yuxin Zhang,Yuchun Wan,Hongbo Zhang,Xiangyu Zou,Chunhui Su

DOI: https://doi.org/10.1016/j.ceramint.2024.06.204

IF: 5.532

2024-01-01

Ceramics International

Abstract:Dy3+, Eu3+ co-doped glass ceramics (GCs) containing SrMoO4 crystalline phase were prepared by melt-curingcrystallization method. The most favorable heat treatment conditions for the glass ceramics were found to be 610 degrees C/2 h by differential scanning calorimetry (DSC), ultraviolet spectrophotometer (UV-Vis), X-ray diffraction (XRD) and scanning electron microscopy (SEM). The best doping concentrations of Dy3+ and Eu3+ in this glass ceramic were 0.8 % and 0.6 %, concentration quenching caused by dipole-dipole interactions occurs when the content of rare earth ions in GCs continues to increase. The chromaticity coordinates of the Dy3+- Eu3+ co-doped glass ceramics changed from cool white light to warm white light with the addition of Eu3+ concentration. At the optimal doping concentration (0.8 % Dy3+-0.6 % Eu3+), the chromaticity coordinate of glass ceramics is (0.3972, 0.3331), and the related color temperature is 3047 K. The luminescence intensity can still reach about 80 % of room temperature at 180 degrees C, and its thermal quenching activation energy is 0.233 eV. This suggests that glass ceramics have excellent thermal stability. After adding an appropriate amount of Li+, the crystalline phase of the glass ceramics remained unchanged and the luminous intensity of the glass ceramics increased by a factor of about 1.4 in the same environment. The thermal quenching activation energy of the glass ceramic doped with 0.2 % Li+-0.8 % Dy3+-0.6 % Eu3+ was 0.344 eV. The experimental results indicate that GCs has potential application prospects in the field of solid-state lighting.