Abstract:Epoxy resin has become one of the most widely used polymers owing to their excellent comprehensive properties. However, the inherent inflammability of epoxy resin (EP) has seriously limited its application in a range of fields with high fire safety requirements. Herein, a novel shell–core hierarchy architecture (DAP@SiO 2 ) was prepared, composed of diammonium hydrogen phosphate (DAP) and in situ grown silica, and its structure and morphology were characterized by electron microscopy and infrared spectroscopy. The results indicated that silica particles were uniformly coated onto the surface of DAP. The modified DAP was used to reinforce the epoxy resin. The thermal stability of the EP blends was studied with the use of thermogravimetric analysis. The diammonium phosphate in DAP@SiO 2 flame retardant produces pyrolysis gases such as NH 3 and N 2 during decomposition, diluting the concentration of oxygen and flammable volatile products around the flame. Secondly, silica migrates to the surface of epoxy resin to form a shielding layer, forming compounds containing Si–O–Si and O–Si–C structures, which can be cross-linked with other condensed phase products, greatly improving the thermal stability of the carbon layer. Fire behavior was evaluated using the limiting oxygen index (LOI), vertical burning test, and the cone calorimetry, and the flame retardancy mode of action was explained. With 12% of DAP@SiO 2 involved, the EP blend passes UL-94 V-0 level, and its limiting oxygen index (LOI) reaches 33.2%. The incorporation of DAP@SiO 2 in an EP matrix showed a slight reduction in the heat release and smoke production. The flame retardant mode of the EP polymer shows that its flame retardant and smoke suppression characteristics are related to the interaction of flame retardants in the gas phase and condensed phase. The mechanical properties test results illustrated that the tensile strength, elastic modulus and impact strength of EP/3%DAP@SiO 2 are improved compared with pure EP. This is due to the crosslinking reaction between a large number of amino groups on the surface of DAP@SiO 2 and the epoxy group on the epoxy resin, which significantly enhances the interfacial compatibility between DAP@SiO 2 and epoxy resin, making the combination of DAP@SiO 2 and epoxy resin closer.

Epoxy Polymers Containing Metal–Organic Framework-Derived Layered Double Hydroxide and Black Phosphorus for Fire Resistance, Smoke Suppression, and Wear Resistance

Innovative design of hierarchical cobalt-based borate functionalized black phosphorus structure with petal-like wrinkle: Enhancing the fire safety and mechanical properties of epoxy resin

Flame protection capability of waterborne epoxy coatings enhanced by inorganic-organic phenyl zirconium phosphate anchored boron nitride

Synergistic effects of aryl diazonium modified Few-Layer black Phosphorus/Ultrafine rare earth yttrium oxide with enhancing flame retardancy and catalytic smoke toxicity suppression of epoxy resin

Breaking the Trade-off Between Mechanical Properties and Fire Safety of Epoxy Resins Based on Phosphaphenanthrene Derivatives by Covalent Crosslinking

Fabrication of layered double hydroxide@ferric decorated polyphosphazene hybrid architecture towards simultaneously improved fire safety, smoke suppression and mechanical strength of epoxy resin

Co-based Metal-Organic Framework with Phosphonate and Triazole Structures for Enhancing Fire Retardancy of Epoxy Resin

Design of New Functional Flame‐Retardant System for High‐Performance Epoxy Thermosets Enabled by Bifunctional Few‐Layer Black Phosphorus and Synergistic Strategy

Preparation of a Cobalt-Based Metal–Organic Framework and Its Application As a Synergistic Flame Retardant in Epoxy Resins

Synthesis of Nitrogen‐rich Black Phosphorus Via a Diazotization Strategy for Efficient Flame Retardancy and Mechanical Properties of Epoxy Resins

Improving the Thermal Stability and Flame Retardancy of Epoxy Resins by Lamellar Cobalt Potassium Pyrophosphate

Improving Fire Resistance of Epoxy Resin Using Electrolytic Manganese Residue-Based Zeolites Modified with Metal–organic Framework Ligands

A core–shell-structured APP@COFs hybrid for enhanced flame retardancy and mechanical property of epoxy resin (EP)

Flower-like Ni-Al/LDH synergistic polyaniline anchored to the carbon sphere surface to improve the fire performance of waterborne epoxy coatings

Epoxy-based multilayers for flame resistant flexible polyurethane foam (FPUF)

Integrated comprehensive protection coating achieved by ligand engineering modulated MXene@LDH heterojunction with anti-corrosion, electromagnetic wave absorption and fire safety

Passivation of Black Phosphorus by Triazine-Based Silica Coating: Hierarchical BP@SiO2-N@Co(OH)2 Structure for Enhanced Fire Safety and Toughness of Unsaturated Polyester Resins

CoFe Oxides‐Coated 2D Black Phosphorus for Flame‐Retardant Nanocoatings with Tunable Mechanical Strength and Efficient Elimination of Toxic Gases

Enhanced flame-retardant and mechanical properties of epoxy resin by combination with layered double hydroxide, Mg2B2O5 whisker, and dodecyl dihydrogen phosphate

Effect of diammonium hydrogen phosphate coated with silica on flame retardancy of epoxy resin

Covalent Organic Framework with Cu-containing Compounds for Enhancing Flame Retardancy and Smoke Suppression Effects on Epoxy Resin