Abstract:Silica coating can effectively solve the stability issue of lead halide perovskite nanomaterials. However, it is difficult to achieve aqueous SiO2 coating on hydrophobic CsPbBr3 nanocrystals (NCs). In this paper, the hydrolysis process of tetramethoxysilane was controlled to get a homogeneous SiO2 coating or a NC/SiO2 Janus structure. In step 1, the Cs4PbBr6 NCs were silanized using partially hydrolyzed tetramethoxysilane (PH-TMOS). During this process, the Si-OH groups which came from PH-TMOS were absorbed onto the surface of the Cs4PbBr6 NCs with the removal of hydrophobic oleic acid (OA) ligands. In step 2, phase transformation from Cs4PbBr6 to CsPbBr3 occurred owing to the injection of water. Meanwhile, further hydrolysis of TMOS took place and generated cross-linked Si-O-Si. Because the silanization in step 1 created lots of growth sites, the condensation of SiO2 was not limited to the interface between water and hexane. After growing for 12 h, the fully covered CsPbBr3@SiO2 capsules were prepared. The anion exchange reactions of the CsPbBr3@SiO2 capsules were studied. Only one even and symmetric PL peak was apparent during the anion exchange process, which was different from the bare CsPbBr3 NCs. This result demonstrated that the SiO2 shell can act as a buffer layer to block the direct contact of CsPbBr3 with the excess PbBr2 precursor in solution. Compared with the CsPbBr3 NCs, CsPbBr3@SiO2 showed better stability in polar solvent and air. A bright green emission was also observed under UV light after 90 days. The successful preparation of CsPbBr3@SiO2 capsules with enhanced stability paves the way for the further development of lead halide perovskite nanomaterials.

Spectral and dynamic analysis of CsPbBr3 perovskite nanocrystals with enhanced water stability using sodium passivation

Synthesis and Improved Photoluminescent Properties and Stability of Bromine‐Rich CsPbBr3 Nanocrystals Via using CTAB as Additive

Dispersion in water of CsPbBr3 perovskite nanocrystals by surface modification

Bright CsPbBr3 Perovskite Nanocrystals with Improved Stability by In-Situ Zn-Doping

Enhanced environmental stability and luminescence performance of CsPbI 3 nanocrystals through SDS passivation and LEuH anchoring

Multidentate ligand passivation enabled enhanced photoluminescence and stability of CsPbBr3 nanocrystals for white light-emitting diodes

Exceptional Stability Against Water, UV Light, and Heat for CsPbBr3@Pb-MOF Composites

Surface passivation of halide perovskite nanocrystals for stable and high purity color conversion

Highly Stable CsPbBr3 Nanocrystal Phosphors by Surface Passivation and Encapsulation

Two-Step Hybrid Passivation Strategy for Ultrastable Photoluminescence Perovskite Nanocrystals

Water‐Assisted Size and Shape Control of CsPbBr3 Perovskite Nanocrystals

Efficient CsPbBr3 nanocrystals light emitting diodes achieved with Na+ modifying

Long-term stable and highly efficient photoluminescence from Sr2+-doped CsPbBr3 nanocrystals in boro-germanosilicate glass

Enhanced Stability of CsPbBr3 Nanocrystals through Al2O3 and Polymer Coating

Stable and Efficient Blue‐Emitting CsPbBr 3 Nanoplatelets with Potassium Bromide Surface Passivation

Synergistic Passivation Inducing Long‐Term Stability for Fluorescent CsPbI 3 Perovskite Nanocrystals

Highly Luminescent and Stable CsPbI3 Perovskite Nanocrystals with Sodium Dodecyl Sulfate Ligand Passivation for Red-Light-Emitting Diodes.

Facial synthesis of highly stable and bright CsPbX3 (X=Cl, Br, I) perovskite nanocrystals via an anion exchange at the water-oil interface

Zinc-halide/phenylbutyrate co-passivation of CsPbX 3 nanocrystals toward efficient and robust luminescence

Room-temperature quaternary alkylammonium passivation toward morphology-controllable CsPbBr3 nanocrystals with excellent luminescence and stability for white LEDs

Controlling the growth of a SiO2 coating on hydrophobic CsPbBr3 nanocrystals towards aqueous transfer and high luminescence