Room-temperature quaternary alkylammonium passivation toward morphology-controllable CsPbBr3 nanocrystals with excellent luminescence and stability for white LEDs

Louwen Zhang,Wenxi Liang,Ling Xu,Meng Zhu,Xi Wang,Jun Su,Luying Li,Nishuang Liu,Zhi Zhang,Yihua Gao
DOI: https://doi.org/10.1016/j.cej.2021.129349
IF: 15.1
2021-08-01
Chemical Engineering Journal
Abstract:<p>Colloidal all-inorganic CsPbX<sub>3</sub> (X = Cl, Br, I) perovskite nanocrystals (PNCs) have recently shown incomparable superiority and vast application prospects in optoelectronics. However, developing low-cost and high-quality PNCs is the priority on their way to commercialization. Herein, we proposed a room-temperature quaternary alkylammonium (didodecyldimethylammonium bromide, DDAB) passivation strategy without organic polar solvents for synthesizing CsPbBr<sub>3</sub> PNCs with controllable morphology via a modified ligand-assisted reprecipitation method. The morphology and size of PNCs were strongly affected by the amount of surface ligands (DDAB and organic acids with different chain lengths), resulting in the shift of emission peak. Benefiting from tight binding of surface ligands, the resulting CsPbBr<sub>3</sub> PNCs exhibited bright green emission with near-unit photoluminescence quantum yields (PLQY) and excellent stability against water and air. The ultrafast transient absorption and time-resolved photoluminescence spectra further revealed that the lifetime of trap-assisted non-radiative recombination in PNCs was especially short, which could be attributed to the efficient passivation of surface defect states. Furthermore, light-emitting diodes (LEDs) based on green PNCs showed bright white light emission, and its corresponding color coordinate (0.330, 0.329) was almost consistent with that of the standard white light, which indicated that the as-prepared PNCs had latent practical value in lighting and display technology.</p>
engineering, chemical, environmental
What problem does this paper attempt to address?
The problems that this paper attempts to solve mainly focus on two aspects: 1. **Improving the fluorescence quantum yield (PLQY) and stability of CsPbBr₃ perovskite nanocrystals (PNCs)**: Although CsPbX₃ (X = Cl, Br, I) perovskite nanocrystals show great application potential in optoelectronic devices due to their excellent optoelectronic properties, non - radiative recombination and low photoluminescence efficiency (PLQY) caused by surface defects as well as poor environmental stability seriously hinder their commercialization process. In this paper, by using quaternary ammonium salts (such as didodecyldimethylammonium bromide, DDAB) for surface passivation at room temperature, the PLQY and environmental stability of CsPbBr₃ PNCs are effectively improved. 2. **Realizing the controllable synthesis of CsPbBr₃ nanocrystal morphology**: By adjusting the amounts of surface ligands (DDAB and organic acids with different chain lengths), precise control of the morphology of CsPbBr₃ PNCs (such as nanorods, nanowires and nanocubes) is achieved. This not only enriches the nanoshapes of such materials but also broadens their application range in lighting and display technologies. ### Specific problem - solving methods - **Surface passivation strategy**: Using DDAB as a surface passivating agent, by tightly binding to the PNCs surface, the surface defect states are effectively reduced, thereby significantly improving the PLQY and stability of PNCs. Experimental results show that the surface - passivated CsPbBr₃ PNCs exhibit a PLQY close to 100% and have excellent water and air stability. - **Morphology control**: By changing the types and amounts of surface ligands (DDAB and organic acids with different chain lengths), the morphology of CsPbBr₃ PNCs is successfully regulated. For example, using organic acids with different chain lengths (C4, C6, C8, C14, etc.) can respectively obtain PNCs with different morphologies such as nanocubes, nanowires and nanorods. ### Experimental results - **Optical properties**: The surface - passivated CsPbBr₃ PNCs exhibit a high PLQY (up to 97.2%) and have a single radiative decay process, indicating that the non - radiative recombination process is almost completely suppressed. - **Stability**: Experimental results show that these PNCs can still maintain strong green fluorescence after being treated in water for 20 days and also show excellent stability after being stored in air for 20 days. In addition, the fluorescence characteristics of PNCs films hardly change after being stored in air for half a year. ### Application prospects - **White LEDs**: White LEDs prepared based on these green PNCs show color coordinates (0.330, 0.329) close to standard white light and have a 128% NTSC color gamut, demonstrating their potential application value in lighting and display technologies. In summary, through innovative surface passivation and morphology control strategies, this paper significantly improves the optical properties and stability of CsPbBr₃ PNCs, laying the foundation for their practical application in optoelectronic devices.