Abstract:This study focuses on promoting the low temperature performance of vanadium-based catalysts; for this, the SHS method was applied to synthesize a series of Ti0.9VxM0.1-xO2-delta catalysts. The performances of the catalysts (Ti0.9V0.1O2-delta, Ti0.9Mn0.05V0.05O2-delta, and Ti0.9Ce0.05V0.05O2-delta), were fully investigated with the temperature-programmed-reaction, which proved that these SHS catalysts with nanometer size had high activity over a broad temperature window of 150-400 degrees C. Compared with Ti0.9V0.1O2-delta, the substituted Catalysts, Ti0.9Mn0.05V0.05O2-delta and Ti0.9Ce0.05V0.05O2-delta, showed higher N-2 selectivity at high temperatures. The Ce substituted catalyst exhibited good resistance to H2O and SO2 poisoning at low temperatures. The structural and physical-chemical properties of catalysts were characterized comprehensively by BET, XRD, FTIR, TEM, EDX, XPS, and TPD. The XRD results indicated that the active components of V, Mn, and Ce were highly dispersed over the catalysts. The Mn substitution could enhance the Bronsted acid sites on the catalyst surface and accelerate the SCR reaction at low temperatures. The XPS shows that the Ce substitution led to high concentration of chemisorbed oxygen, which diminished the unselective oxidation of NH3 by O-2 to N2O, NO, or NO2 and resulted in superior N-2 selectivity. The active components of the catalysts, such as V, Mn, and Ce, mostly existed in the form of mixed-valence which was beneficial for the oxidation of NO to NO2. Furthermore, the SCR reaction mechanism over Ti0.9Ce0.05V0.05O2-delta catalyst was also examined using in situ DRIFTS. The results revealed that high active monodentate,e nitrate and bridging nitrate species as well as abundant ionic NH4+ (Bronsted acid sites) were the key intermediates in the SCR reaction since the ad-monodentate nitrate and bridging nitrate species disappeared quickly in the presence of NH3.

Simultaneous Removal of Naphthalene and NOx over V-Ce/Ti Catalyst: Design of Separated Active Sites for Naphthalene Degradation and SCR Reaction

In Situ DRIFTS Studies of NH3-SCR Mechanism over V2O5-CeO2/TiO2-ZrO2 Catalysts for Selective Catalytic Reduction of NOx

Design of bimetallic catalyst with dual-functional Cu-Ce sites for synergistic NO X and toluene abatement

Remarkable Enhancement in the N-2 Selectivity of NH3-SCR over the CeNb3Fe0.3/TiO2 Catalyst in the Presence of Chlorobenzene

Interaction Mechanism for Simultaneous Elimination of Nitrogen Oxides and Toluene over the Bifunctional CeO2-TiO2 Mixed Oxide Catalyst

Performance of Ce-modified V-W-Ti type catalyst on simultaneous control of NO and typical VOCS

Selective Catalytic Reduction of NOx with NH3 over Mn, Ce Substitution Ti0.9V0.1O2−δ Nanocomposites Catalysts Prepared by Self-Propagating High-Temperature Synthesis Method

Remarkable enhancement in the N2 selectivity of NH3-SCR over the CeNb3Fe0.3/TiO2 catalyst in the presence of chlorobenzene

Selective catalytic reduction of NO<sub>x</sub> with NH<sub>3</sub> over a novel Co-Ce-Ti catalyst

Promotional Effect of Ce-Doped V2o5-Wo3/Tio2 with Low Vanadium Loadings for Selective Catalytic Reduction of Nox by Nh3

Synergistic Removal of NO and N 2 O in Low-Temperature SCR Process with MnO X /ti Based Catalyst Doped with Ce and V

VxMn(4-x)Mo3Ce3/Ti catalysts for selective catalytic reduction of NO by NH3

The modification of surface basicity and its role in naphthalene oxidation: The effect of the basic sites introduced by Ce

The activity and characterization of CeO2-TiO2 catalysts prepared by the sol-gel method for selective catalytic reduction of NO with NH3.

Simultaneous removal of NO and dichloromethane (CH2Cl2) over Nb-loaded cerium nanotubes catalyst

The selective catalytic reduction of NO over Ce0.3TiOx-supported metal oxide catalysts

TiO2-modified CeVO4 catalyst for the selective catalytic reduction of NOx with NH3

Effect of Ce Doping into V2O5-WO3/TiO2 Catalysts on the Selective Catalytic Reduction of NOx by NH3

Ti species regulated CuO/CeO2 catalyst for efficient simultaneously NH3-SCR denitration and CO oxidation under oxygen-rich conditions

Investigation of the SCR Catalyst Ce-V/TiO<sub>2</sub>

Selective Catalytic Removal of High Concentrations of NOx at Low Temperature