Extensive screening and performance testing of nucleating agents for the sodium acetate trihydrate phase-change material

Christoph Salzmann,Jinjie Li,Michael Parkes

DOI: https://doi.org/10.26434/chemrxiv-2024-h5zqj

2024-05-29

Abstract:Heat batteries often rely on phase-change materials that undergo phase transitions upon heat charging and release. Sodium acetate trihydrate (SAT) is considered one of the best phase-change materials in terms of storage capacity. Yet, it is well-known for supercooling which makes the search for effective nucleating agents a high priority. To perform extensive screening for nucleating agents and to test their performance, we designed a new instrument. The HeatMaster is capable of analyzing six samples on the gram-scale in parallel using the principle of power compensation which means that heat releases and uptakes can be obtained in a quantitative fashion. Out of the 36 tested nucleating agents, CaCl2·2H2O was identified as the best nucleating agent that outperforms several of the previously known nucleating agents in terms of temperature range of operation up to 80 °C. CaCl2·2H2O performs reliably as a nucleating agent for SAT down to 0.5 weight percent. MgCl2·6H2O was also identified as a nucleating agent. Yet, similar to the well-known Na2HPO4∙12H2O, its performance is not reliable after heating to 80 °C. Out of the three nucleating agents, CaCl2·2H2O shows the best performance with respect to deterioration of the heat releases upon extensive thermal cycling with a maximum temperature of 65 °C.

Chemistry

What problem does this paper attempt to address?

This paper focuses on the supercooling issue encountered when using sodium acetate trihydrate (SAT) as a phase change material in thermal batteries. The researchers designed a new instrument called HeatMaster for large-scale screening and testing of nucleating agents to address the supercooling phenomenon of SAT and improve its performance in thermal energy storage. Through testing 36 different nucleating agents, they found that CaCl2·2H2O was the most effective nucleating agent, capable of operating at temperatures as high as 80°C and exhibiting stability at a concentration of 0.5 weight percent. In contrast, MgCl2·6H2O was also identified as a nucleating agent, but its performance became unreliable after heating to 80°C. Additionally, the study explored challenges such as degradation of nucleating agent performance over time, inconsistent melting, and phase separation, and experimentally determined the optimal quantity of CaCl2·2H2O as a nucleating agent. This research aims to provide a more stable and efficient phase change material solution for the design and optimization of thermal batteries.