Core–Shell Co, Zn Bimetallic Selenide Embedded Nitrogen-Doped Carbon Polyhedral Frameworks Assist in Sodium-Ion Battery Ultralong Cycle
Zheng Zhang,Ying Huang,Xudong Liu,Xin Wang,Panbo Liu
DOI: https://doi.org/10.1021/acssuschemeng.0c02521
2020-05-20
Abstract:Sodium-ion batteries (SIBs) have become the best alternative to lithium-ion batteries. However, it is difficult to meet the efficiency of SIBs using graphite. Transition-metal selenides are expected to be ideal anode materials for SIBs, but some problems still need to be solved, such as poor conductivity and volume expansion. Here, we successfully synthesized a core–shell structure <sub>2</sub>/NC composite using as a precursor. The in situ decorated ZnSe and CoSe<sub>2</sub> nanoparticles on the NC polyhedral framework provide a rich active site for the entire electrode. In addition, the NC can simultaneously increase the conductivity and alleviate the volume effect generated during the cycling process. The <sub>2</sub>/NC composites exhibit excellent electrochemical performance when used in SIB anode materials. When the current density is 0.1 A g<sup>–1</sup>, the reversible capacity is 499.1 mA h g<sup>–1</sup> after 100 cycles. When the current density is increased to 1.0 A g<sup>–1</sup>, a reversible capacity of 273.5 mA h g<sup>–1</sup> after 4000 cycles is delivered. In addition, the <sub>2</sub>/NC composite also exhibits superior rate performance. The sodium reaction kinetics of the <sub>2</sub>/NC composite was analyzed to explain its outstanding electrochemical performance. These results reveal the enormous potential of <sub>2</sub>/NC composites in building efficient SIBs.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acssuschemeng.0c02521?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acssuschemeng.0c02521</a>.Experimental: (a) XRD pattern of ZIF precursor; TEM images of (b) ZIF-8, (c) ZIF-67, and (d) ; SEM images of (e) ZIF-8, (f) ZIF-67, and (g) (Figure S1). (a) TEM images and EDS mapping, (b) HRTEM, (c) elemental line scan, and (d) EDS spectrum of ZnSe/NC; (e) TEM images and EDS mapping, (f) HRTEM, (g) elemental line scan, and (h) EDS spectrum of CoSe<sub>2</sub>/Nc (Figure S2). BET curves and BJH pore size distribution of (a) and (c) ZnSe/NC and (b) and (d) CoSe<sub>2</sub> (Figure S3). CV curves of (a) CoSe<sub>2</sub>/NC and (b) ZnSe/NC and (c) the combined third cycle CV curves of ZnSe/NC, CoSe<sub>2</sub>/NC, and <sub>2</sub>/NC; discharge–charge curves of (d) ZnSe/NC, (e) CoSe<sub>2</sub>/NC, and (f) <sub>2</sub>/NC at a current density of 0.1 A g<sup>–1</sup>; and (g) equivalent circuit used for fitting the experimental data (Figure S4). CV curves of (a) ZnSe/NC and (d) CoSe<sub>2</sub>/NC at different scan rates; log(<i>i</i>) vs log(<i>v</i>) plots at specific peak currents of (b) ZnSe/NC and (e) CoSe<sub>2</sub>/NC; and CV curve of (c) ZnSe/NC and (f) CoSe<sub>2</sub>/NC with capacitance contribution shown in the shaded area at 0.1 mV s<sup>–1</sup> (Figure S5). Specific surface area, total pore volume, and mean pore diameter of the as-prepared materials (Table S1). Electrochemical impedance values of three electrode materials (Table S2). Comparison of the cycle performance of these materials as anode materials of SIBs (Table S3) (<a class="ext-link" href="/doi/suppl/10.1021/acssuschemeng.0c02521/suppl_file/sc0c02521_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology