Abstract:Sodium-ion batteries (SIBs) have been acknowledged as a particularly promising supplement to lithium-ion batteries, thanks to the abundant sodium resources, geographically-wide distribution and low cost. However, the large volume expansion hence poor structural stability of the anode in the Na + insertion/deinsertion process severely compromises the rate performance of SIBs. Herein, we report the hierarchical, hollow structured nanocages of nickel-cobalt bimetallic selenide covered by nitrogen-doped carbon shell (NiCo 3 Se 4 @NC) as anode material for SIB. The hollow structure and the abundant holes on the cage walls greatly shorten the transfer distance for Na + ions and buffer the volume expansion during the Na + storage process. The bimetallic form expands the lattice spacing meanwhile increase the density of states near Fermi level. Moreover, the highly-conductive NC shell further benefits the charge transfer and structural stability upon Na + storage, and promotes the cycle stability. As a result, surface-responsive capacitive-dominated kinetic process is revealed from the NiCo 3 Se 4 @NC anode, delivering a high reversible capacity of 416 mAh g –1 at a current density of 0.05 A g –1 and 314 mAh g –1 at 2 A g –1 . This work proposes an efficient strategy to substantially increase the rate performance and cycle stability of SIBs.

Bimetallic selenide nanocages covered by carbon layer deliver high rate performance for sodium ion storage