GOLD RECOVERY FROM WASTE PRINTED CIRCUIT BOARD IODIDE LEACHATES USING A NOVEL MEMBRANE-BASED ELECTROWINING PROCESS

Ngeleka Marco Mukuna,Jochen Petersen ,Thandazile Moyo

DOI: https://doi.org/10.26434/chemrxiv-2024-z139t

2024-05-28

Abstract:The hydrometallurgical recovery of gold from waste printed circuit boards is considered a promising recycling technique. This paper presents the findings from a study investigating the feasibility of a hydrometallurgical technique to recover gold from waste printed circuit board iodide leachates using a novel membrane-based electrowinning process. Findings showed that the investigated novel process has the potential to be technically feasible if employed in a real-life industrial-scale waste printed circuit board recycling operation. This is primarily because high purity (>99%) Au was effectively recovered using the investigated process with a 95.50 % yield under the following conditions: 6.0 hrs time, constant cell voltage of 12.9 V, temperature of 25 degrees celsius, 250 rpm agitation speed, average current of 5 A, 1429 A/m2 equivalent current density, and 8.4 × 10-6 mol/m2.s Au flux. Overall, the simultaneous recovery of iodide lixiviant with Au makes the recovery process simple as well as potentially cost-effective. Further studies on the process scale-up are required to accurately evaluate the overall costing of the gold recovery process via the proposed technology.

Chemistry

What problem does this paper attempt to address?

This paper aims to solve the problem of efficiently recovering gold (Au) from iodide leachate of waste printed circuit boards (WPCB). Specifically, the research explored the feasibility of a new membrane - based electrodeposition technology in actual industrial - scale WPCB recovery operations. Through this technology, researchers hope to achieve effective recovery of high - purity (> 99%) gold without using expensive and environmentally - harmful traditional metallurgical methods. The study found that under specific conditions (such as 6 hours, a constant cell voltage of 12.9 V, a temperature of 25 °C, a stirring speed of 250 rpm, an average current of 5 A, a current density of 1429 A/m², and a gold flux of 8.4 × 10⁻⁶ mol/m²·s), a gold recovery rate of 95.50% can be achieved. In addition, the simultaneous recovery of iodinating agents and gold makes the entire recovery process simpler and potentially more cost - effective. However, in order to more accurately assess the cost of the entire gold recovery process, further research is needed to expand the process scale.