Preparation of Natural Bio-Based Eucommia Ulmoides Gum/styrene-Butadiene Rubber Composites and the Evaluation of Their Damping and Sound Absorption Properties
Renwei Cao,Linhui Deng,Zhibo Feng,Xiuying Zhao,Xiaolin Li,Liqun Zhang
DOI: https://doi.org/10.1016/j.polymer.2020.123292
IF: 4.6
2021-01-01
Polymer
Abstract:To achieve effective sound absorption in wide frequency bands under high pressures, Eucommia ulmoides gum (EUG) as one of the natural biopolymers was incorporated into styrene-butadiene rubber (SBR) to prepare sound absorption materials. The morphology, crystalline structure, and macro-performance (damping, sound absorption, and mechanical properties) of the as-produced composites were systemically investigated. When the EUG content was less than 30 phr, the EUG was dispersed in the SBR matrix as nanocrystallites primarily existed in the beta-crystal form, which is demonstrated by wide-angle X-ray diffraction (WAXD) and polarizing microscope (POM). The dynamic mechanical thermal analyzer (DMA) results expressed that EUG had two dynamic mechanical loss peaks, i.e. the glass transition peak (Peak 1, -60-40 degrees C) and melting transition peak (Peak 2, 30-60 degrees C). Thus, the addition of EUG improved the damping performance of the composites in high-temperature areas to some extent. Moreover, in comparison to the neat SBR, the average sound absorption coefficient of SBR/ EUG (70/30) composite increased by 24.23% in the frequency range of 3-8 kHz under 2.5 MPa, which show the excellent sound absorption properties. And since the EUG nanocrystallites played the role of physical crosslingking points, the SBR/EUG (70/30) composite also had outstanding comprehensive mechanical properties. The SBR/EUG composites may be applied to underwater sound absorption materials.