Radiation-induced Grafting of Polyethyleneimine Onto Cellulose Triacetate Membrane for Separation of Cesium Ions from Aqueous Solution

Jinling Wu,Jianlong Wang

DOI: https://doi.org/10.1016/j.radphyschem.2024.111832

IF: 2.776

2024-01-01

Radiation Physics and Chemistry

Abstract:Radiation grafting of polyethyleneimine (PEI) onto the surface of cellulose triacetate (CTA) membrane was successfully performed. Pre-radiation and co-radiation were applied by gamma rays at the dose of 12 kGy. FT-IR, SEM, XPS, contact angle, zeta-potential, grafting ratio, etc. were used to characterize the PEI-CTA membranes before and after grafting. The FT-IR spectrum showed that a notable discernable shoulder peak of N-H appeared for amide at co-radiation and pre-radiation, and XPS analysis indicated that co-radiation achieved the highest N percent of 9.75%, suggesting that PEI was introduced into the membrane surface. In a forward osmosis (FO) process, the PEI-CTA membrane obtained higher cesium, Cs(I), retention (95-97%) than the CTA membrane with Cs(I) retention of 92%. Cs(I) fluxes significantly decreased from 0.09 to 0.02-0.03 mmol m-2h-1 after PEI modification. Effective Cs(I) retention was attributed to increase of the positive charges on CTA membrane when PEI was added, which exerted a repulsive effect on Cs(I), preventing them from moving towards the membrane direction. In the FO process, the PEI-CTA membrane featured the water flux of 23 L m-2 h-1 a little lower than that of CTA membrane (24 L m-2 h-1). Although modified PEI increased the hydrophilicity, the increase of water flux did not occur with the co-irradiated membrane, which was related to the high graft, higher thickness and resistance of the membrane.