Abstract:Hot-stamped ultrahigh strength steel components are pivotal to automotive light-weighting. Steel blanks, often coated with an aluminum-silicon (Al-Si) layer to protect them from oxidation and decarburization, are austenitized within a furnace and then simultaneously quenched and formed into shape. The Al-Si coating melts within the furnace and reacts with iron from the steel to yield an intermetallic phase that provides some long-term corrosion protection. During the intermediate liquid phase, some of the coating may transfer to the furnace components, leading to maintenance costs and operational downtime. A detailed understanding of the coating transformation mechanism is needed to avoid such production issues while ensuring that final intermetallic coatings conform to specifications. We introduce cross-sectional Raman microscopic mapping as a method to rapidly elucidate the coating transformation mechanism. Raman spectroscopic fingerprints for relevant intermetallic compounds were determined using synthesized Al-Fe-Si ternary and Al-Fe binary compounds. These fingerprints were used to map the spatial distribution of intermetallic compounds through cross sections of Al-Si-coated 22MnB5 specimens that were heated at temperatures between 570 and 900 °C. These chemical maps show that the intermetallic fraction of the coating does not grow significantly until formation of η (Al5Fe2) at the steel interface, suggesting that η facilitates extraction of iron from the steel and subsequent diffusion through the coating. Under the heating conditions used here, a series of reactions ultimately lead to a silicon-rich τ2 (Al3FeSi) phase on top of the binary η phase. The technique presented here simplifies structural analysis of intermetallic compounds, which will facilitate prototyping of strategies to optimize hot stamping.

Phase Transformation and Microstructural Evolution of Coating Layer of Al–Si Coated 22mnb5 Steel During Thermal Diffusion

The Effect of Heat Treatments on the Microstructural Evolution of Twin-Roll-Cast Al-Fe-Si Alloys

Effects of Heat Treatments on Phase Structure of Electrodeposition Aluminum Coatings on Different Substrates

Phase Composition of Al-Si Coating from the Initial State to the Hot-Stamped Condition

Phases Formation and Evolution at Elevated Temperatures of Al–12Si–3.8Cu–2Ni–1Mg Alloy†

Structure and High-Temperature Oxidation Performance of Si-Co Diffusion Coatings Prepared on a TiAl-Nb Alloy

A comprehensive investigation of phase evolution of Al-Si coating during the prolonged aging at 650 °C

Raman Spectroscopic Analysis of the Reaction between Al-Si Coatings and Steel

Microstructure Characteristics of Fe-Al Intermetallic Compound Coating Synthesized by Light Beam Alloying

Research on high-temperature oxidation resistance, hot forming ability, and microstructure of Al–Si–Cu coating for 22MnB5 steel

Microstructural evolution and element interdiffusion of NiAlHf and NiAlHfY coatings deposited on a Ni-based superalloy

Abnormal phase evolution and degradation behavior of Al-Si coating during 30,000 h aging

Thermal stability of Al–Fe–Ni alloy at high temperatures

The phase transition and microstructure of Fe-Co-B alloy films

Phase Transformation in Co-, Mn-, and Al-doped Iron Disilicide Alloys

Characterisation of Fe Distribution in the Liquid–Solid Boundary of Al–Zn–Mg–Si Alloy Using Synchrotron X-ray Fluorescence Microscopy

Influence of Heat Treatment on the Microstructure and Wear Properties of Arc-Sprayed FeCrAl/Al Coating

Interdiffusion and Phase-Formation During Thermal-Processing of Co/Ti/Si(100) Structures

Interdiffusion mechanism at the interface between TiAl alloy and NiCoCrAlY bond coating

Investigation of the Role of Silicon in TiAlSiN Coating Deposited on TiAl Alloys during Long-term Oxidation

Diffusion Modelling on the Microstructure Evolution in MCrAlY-Superalloy System