Perovskite Structure LaNi0.5Fe0.5O3 Electrocatalyst for Rechargeable Li-O2 Batteries

Lili Liu,Yun Feng,Dongdong Wang,Heng Zhang,Yue Liu,Liu Pei,Xindong Wang

DOI: https://doi.org/10.1007/s10562-024-04655-5

IF: 2.936

2024-01-01

Catalysis Letters

Abstract:Developing efficient O2 electrocatalyst is crucial for lithium-oxygen (Li-O2) batteries (LOBs). Among various catalysts, perovskite oxides have exhibited diverse catalytic activity owing to their low synthetic cost, tunable constitutions, flexible structures and excellent electrochemical stability. In this research, LaNi0.5Fe0.5O3 perovskites (LNFO) were synthesized via a classical sol–gel route combined with succedent calcination treatment. The ORR and OER tests indicate that the catalytic activity of LNFO calcined at 600 (LNFO-1) and 800℃ (LNFO-3) is superior to that of 700 (LNFO-2) and 900℃ (LNFO-4). To determine which sample is more suitable as a catalyst for LOBs, the LOBs with LNFO-1 and LNFO-3 electrodes were assembled. The LNFO-1 cathode shows discharge capacity of 1.7686 mAh under the current density of 100 mA g−1, which is higher than that with LNFO-3 cathode. The initial discharge–charge profiles of LOBs with LNFO-1 and LNFO-3 electrodes under a cutoff capacity of 1 mAh at 100 mA g−1 indicates that a lower overpotential could gained from LNFO-1 electrode. Meanwhile, 233 and 93 cycles can be realized under capacity limit of 0.15 and 0.315 mAh, respectively, at the current density of 100 mA g−1. The results demonstrate a lower overpotential, and longer circularity can be implemented in the LOB with LNFO-1 cathode, which can be put down to the larger specific surface area, and more presence of Ni3+ and Fe4+ in LNFO-1. Therefore, our work confirmed that the mesoporous LNFO-1 is a promising electrocatalyst for LOBs.