Formation/Decomposition of Li 2 O 2 Induced by Porous NiCeO x Nanorod Catalysts in Aprotic Lithium–Oxygen Batteries
Yihao Liu,Kun Wang,Xiaohui Peng,Chen Wang,Weiwei Fang,Yusong Zhu,Yuhui Chen,Lili Liu,Yuping Wu
DOI: https://doi.org/10.1021/acsami.2c00545
2022-03-31
Abstract:To realize the utilization of high-performance lithium–oxygen batteries (LOBs), a rational-designed cathode structure and efficient catalytic materials are necessary. However, side products accumulated during battery cycling seriously affects the performance. Designing a cathode catalyst that could simultaneously facilitate the catalytic efficiency of the main reaction and inhibit the side reactions will make great sense. Herein, NiCeOx was proposed for the first time as a bifunctional cathode catalyst material for LOBs. The combined action of NiO and CeO2 components was expected to facilitate the decomposition of byproducts (e.g., Li2CO3), increase the oxygen vacancy content in CeO2, and enhance the adsorption of oxygen and superoxide. NiCeOx nanorods (NiCeOx PNR) were prepared using electrospinning method. It showed a hollow and porous nanorod (PNR)-like structure, which provided a large number of catalytic active sites and facilitated the transport of reactants and the deposition of discharge products. As a result, a high specific discharge capacity (2175.9 mAh g–1) and a long lifespan (67 cycles at 100 mA g–1 with a limited capacity of 500 mAh g–1) were obtained.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsami.2c00545.Synthesis of NiO and CeO2, SEM and TEM images of NiCeOx PNRs, XPS patterns of the NiCeOx PNR (Ni/Ce = 24/1), LSVs of the ORR for different catalysts in 0.1 M KOH electrolyte: (a) Ni/Ce = 5/1 catalyst, (b) Ni/Ce = 9/1 catalyst, (c) Ni/Ce = 5/1 catalyst, and (d) Ni/Ce = 24/1 catalyst, discharge–charge curves for the selected cycles of NiO, CeO2 Super P, Ni/Ce = 5/1, and Ni/Ce = 9/1 catalysts with a capacity limitation of 500 mAh g–1 at a current of 100 mA g–1 (PDF)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology