Abstract:A comprehensive modeling framework for the thermoforming of polymer matrix woven laminate composite was developed. Two numerical indicators, the slip path length and traction magnitude, have been identified to be positively correlated to matrix smearing and wrinkling defects. The material model has been calibrated with picture-frame experimental results, and the prediction accuracy for intra-ply shear and thickness distribution was examined with measurements of the physically formed parts. Specifically, thickness prediction for most locations on the formed parts was accurate within an 11.6% error margin. However, at two points with significant intra-ply shear, the prediction errors increased to around 20%. Finally, a parametric study was conducted to determine the relationship between various process parameters and the quality of the formed part. For the trapezoidal part, orienting the laminate at 45 degrees to the mold axis reduces the likelihood of matrix smear and wrinkling defects. Although this laminate orientation yielded a greater spatial variation in part thickness, the thickness deviation is lower than that for the 0-degree orientation case. Two forming analyses were conducted with ramp rates of 25 mm/s and 80 mm/s to match the equipment's operational limits. It was observed that higher forming rates led to a greater likelihood of defects, as evidenced by a 15% and 10% increase in the formed part areas with longer slip paths and higher traction magnitudes, respectively. It was discovered that shallower molds benefit from faster ramp rates, while deeper molds require slower rates to manage extensive shearing, stretching and bending. Faster forming rates lead to smaller thickness increases at high intra-ply shear regions, indicating a shift from intra-ply shear to out-of-plane bending due to the visco-plastic effect of the molten laminate and can negatively impact part quality. Lastly, it was shown that a well-conceived strategy using darts could improve the part quality by reducing the magnitude of the defect indicators.

Analyses of Wrinkling Mechanisms During Forming of Multi-Layer Woven Fabric Reinforced Thermoplastic Prepregs

Understanding the Impact of Fibre Wrinkle Architectures on Composite Laminates Through Tailored Gaps and Overlaps

Influences of Wrinkles Induced by Tows’ Offset in Automated Fiber Placement on the Bending Properties of Composites

Process-dependent Wrinkle Formation for Steered Tow During Automated Fiber Placement: Modeling and Experimental Verification

Damage and Failure Mechanisms of CFRP Due to Manufacturing Induced Wrinkling Defects

Inter-Ply Slipping Behaviors and Kinetic Equation of Carbon Fiber-Reinforced Epoxy Prepregs for Hot Diaphragm Preforming

A Modeling Framework for the Thermoforming of Carbon Fiber Reinforced Thermoplastic Composites

Characterization of wrinkle morphologies by surface waviness evaluation method during deep forming of multilayer composite preforms

YIELD POINT AND STRESS RELAXATION BEHAVIOR OF PLY-PLY INTERACTION OF THERMOSET PREPREGS

Characterization of tool-ply friction behavior for treated jute/PLA biocomposite prepregs in thermoforming

Plastic wrinkling prediction in thin-walled part forming process: A review

Deformation and Fracture Mechanisms of Automated Fiber Placement Pre-Preg Laminates under Out-of-plane Tensile Loading

An accurate forming model for capturing the nonlinear material behaviour of multilayered binder-stabilised fabrics and predicting fibre wrinkling

A hybrid lamination model for simulation of woven fabric reinforced thermoplastic composites solid-state thermo-stamping

A Mesoscopic Analytical Model to Predict the Onset of Wrinkling in Plain Woven Preforms under Bias Extension Shear Deformation

An experimental and computational investigation of embedded wrinkle's impacts on the compressive responses of thick unidirectional glass fiber-reinforced composites

Multi-scale finite element simulation of the thermoforming of a woven fabric glass fiber/polyetherimide thermoplastic composite

Efficient numerical analysis of in-plane compression-induced defects in thick multi-ply woven textile preforms during double diaphragm forming

Temperature-Dependent modelling of tension, in-Plane shear, and bending behaviour in non-isothermal thermo-Stamping process simulation of unidirectional UHMWPE fibre reinforced thermoplastic TPU composites

Research on the establishment and influence mechanism of critical wrinkling limit diagram (WLD) of plate and shell forming under mold constraints

Numerical and Experimental Investigation of Wrinkling Pattern for Aerospace Laminated Membrane Structures