Crystal structure of a high-pressure/high-temperature phase of alumina by in situ X-ray diffraction
Jung-Fu Lin,Olga Degtyareva,Charles T. Prewitt,Przemyslaw Dera,Nagayoshi Sata,Eugene Gregoryanz,Ho-kwang Mao,Russell J. Hemley
DOI: https://doi.org/10.1038/nmat1121
IF: 41.2
2004-01-01
Nature Materials
Abstract:Alumina (α-Al 2 O 3 ) has been widely used as a pressure calibrant in static high-pressure experiments 1 , 2 , 3 , 4 and as a window material in dynamic shock-wave experiments 5 , 6 , 7 , 8 , 9 , 10 , 11 , 12 , 13 , 14 ; it is also a model material in ceramic science. So understanding its high-pressure stability and physical properties is crucial for interpreting such experimental data, and for testing theoretical calculations 15 , 16 , 17 , 18 , 19 , 20 , 21 . Here we report an in situ X-ray diffraction study of alumina (doped with Cr 3+ ) up to 136 GPa and 2,350 K. We observe a phase transformation that occurs above 96 GPa and at high temperatures. Rietveld full-profile refinements show that the high-pressure phase has the Rh 2 O 3 (II) ( Pbcn ) structure, consistent with theoretical predictions 22 . This phase is structurally related to corundum, but the AlO 6 polyhedra are highly distorted, with the interatomic bond lengths ranging from 1.690 to 1.847 Å at 113 GPa. Ruby luminescence spectra from Cr 3+ impurities within the quenched samples under ambient conditions show significant red shifts and broadening, consistent with the different local environments of chromium atoms in the high-pressure structure inferred from diffraction. Our results suggest that the ruby pressure scale needs to be re-examined in the high-pressure phase, and that shock-wave experiments using sapphire windows need to be re-evaluated.