Operando Photoelectron Spectroscopy Analysis of Li6PS5Cl Electrochemical Decomposition Reactions in Solid-State Batteries

Burak Aktekin,Elmar Kataev,Luise M. Riegger,Raul Garcia-Diez,Zora Chalkley,Juri Becker,Regan G. Wilks,Anja Henss,Marcus Bär,Jürgen Janek

DOI: https://doi.org/10.26434/chemrxiv-2024-g4wkt

2024-04-17

Abstract:Most solid electrolytes (SEs) which are promising for all-solid-state battery (ASSB) applications are known to have a narrow electrochemical stability window. Consequently, parasitic electrolyte reactions are observed when high-energy-density electrode materials such as lithium and silicon are employed, hindering their utilization in commercial battery systems. Therefore, it is crucial to understand at which potentials such reactions start, and which chemical species are present in the subsequently formed solid electrolyte interphase (SEI). Herein, a new operando experimental approach is introduced to investigate such reactions by employing hard X-ray photoelectron spectroscopy (HAXPES). This approach enables the examination of the SEI formed below a thin metal film (e.g., 6 nm nickel) acting as the working electrode. The feasibility of this approach is demonstrated using a sulfide-based Li6PS5Cl solid electrolyte (lithium argyrodite). It is shown that electrolyte reduction reactions start upon polarization of the working electrode to voltages below 1.75 V (vs. Li+/Li) and result in considerable Li2S formation, particularly in the voltage range of 1.5 – 1.0 V. The overall intensity trends confirm the heterogeneous/layered microstructure of the SEI (e.g., preferential Li2O and Li2S deposition near the current collector). The reversibility of side reactions is also observed, as Li2O and Li2S decompose in the 2–4 V potential window, generating oxidized sulfur species, sulfites and sulfates. The introduced experimental approach is promising for the spectroscopic investigation of electrolyte side reactions under dynamic conditions for various solid electrolyte and current collector combinations.

Chemistry

What problem does this paper attempt to address?

The paper attempts to address the issue of the electrochemical decomposition reactions of sulfide solid electrolytes (such as Li6PS5Cl) at low potentials in all-solid-state batteries and the chemical composition and structural characteristics of the solid electrolyte interface (SEI) formed. Specifically, the researchers aim to understand at which potentials these electrolytes begin to decompose and what chemical substances exist in the formed SEI.

### Background and Motivation
1. **Advantages of All-Solid-State Batteries**: All-solid-state batteries (ASSBs) are considered important candidates for next-generation battery technology due to their high energy density, safety, cost-effectiveness, and environmental friendliness.
2. **Electrolyte Stability Issues**: Most sulfide solid electrolytes are unstable at low potentials (e.g., the operating potential of lithium metal anodes), leading to electrolyte decomposition reactions and the formation of SEI or mixed conductive interfaces (MCI).
3. **Impact of SEI**: The formation of SEI can lead to lithium inventory loss and hinder lithium transport kinetics, thereby affecting the cycle life of the battery.

### Research Methods
1. **Experimental Method**: The researchers introduced a new in-situ experimental method using hard X-ray photoelectron spectroscopy (HAXPES) to study these reactions. This method allows the analysis of the SEI formation process under actual operating conditions using a thin metal film (e.g., 6 nm nickel) as the working electrode.
2. **Experimental Design**: A 6 nm thick nickel film was coated on the surface of the Li6PS5Cl electrolyte pellet to serve as the working electrode. Lithium metal was used as the counter and reference electrode. By gradually polarizing the working electrode to different potentials, the decomposition reactions of the electrolyte were observed.

### Main Findings
1. **Onset Potential of Electrolyte Decomposition**: The reduction reaction of the electrolyte starts at 1.75 V (relative to Li+/Li) and significantly forms Li2S in the voltage range of 1.5 to 1.0 V.
2. **Microstructure of SEI**: The SEI was observed to have a heterogeneous/layered microstructure, with preferential deposition of Li2O and Li2S particularly near the current collector region.
3. **Reversibility**: Within the potential window of 2 to 4 V, Li2O and Li2S can decompose, forming sulfur oxides, sulfites, and sulfates.

### Significance
1. **Understanding SEI Formation Mechanism**: Through in-situ HAXPES technology, researchers can gain detailed insights into the SEI formation process, which is crucial for designing more stable anode/electrolyte interfaces.
2. **Optimizing Battery Performance**: These findings help in developing improved all-solid-state battery systems, enhancing their cycle stability and overall performance.

In summary, this paper delves into the electrochemical decomposition behavior of sulfide solid electrolytes in all-solid-state batteries using advanced in-situ characterization techniques, providing important scientific evidence for designing high-performance all-solid-state batteries.