Hydrogen Blistering and Cracking of High-Strength Pipeline Steel Welds Produced by Electrochemical Hydrogen Charging

Liangyun Lan,Yiting Zhang,Zhiyuan Chang,Huixing Li,Jiyao Yin,Andrej Atrens
DOI: https://doi.org/10.1016/j.mtla.2024.102091
2024-01-01
Materialia
Abstract:Pipeline steel system always faces a challenge of hydrogen embrittlement (HE) not only due to corrosion environments but also because of cathodic protection strategy. Especially in welded joint, heterogeneous microstructures lead to the difference in intrinsic HE resistance for different subzones. However, this aspect was often neglected when external loading was applied during evaluation of the HE. To eliminate the effect of external loading, the hydrogen damage behaviors of X100 pipeline steel weld were investigated only based on electrochemical hydrogen charging and the intrinsic HE resistance of each subzone was explored. The results showed that the HE resistance of the main regions in weld was decreased in order of weld metal, heat affected zone (HAZ) and base metal (BM), with different surface damage modes: the BM had predominantly hydrogen blistering; while others displayed mainly hydrogen cracking. The corresponding features for cross-sectional cracking were intergranular propagation along the pancaked grain boundaries in the BM and trangranular propagation in HAZ. For transgranular cracking propagation, the path first trended to initiate on the {100} cleavage plane, then grew on the {110} slip planes. The intergranular cracking was mainly attributed to the lamellar-structural prior grain boundaries that inherited numerous deformation dislocations during hot rolling of the base metal.
What problem does this paper attempt to address?