Correlation of Rheological Properties with Porosity and Strain Hardening Criterion of High Ductility Cementitious Composites

Xiang-peng Fei,Li-Ping Guo,Ying-jie Chu,Bang-cheng Lyu,Hai-tao Chen

DOI: https://doi.org/10.1016/j.conbuildmat.2024.135972

IF: 7.4

2024-01-01

Construction and Building Materials

Abstract:The high ductility of high ductility cementitious composites (HDCC) relies on both fiber dispersion uniformity and defect size distribution. While fiber dispersion is often prioritized in HDCC design, the impact of defect distribution, particularly pore structure, is overlooked. Correspondingly, there is scant information available on the connection between pore structure and mechanical properties of high ductility cementitous composites under rheological adjusting. This paper aims to explore the correlation between rheological properties, pore structure, and mechanical characteristics of HDCC. By adjusting fly ash (FA) dosage, water-binder ratio (W/B), and additive dosage, rheological properties are modified to optimize fiber dispersion and pore structure. Results show that increased harmful porosity (>20 nm) correlates with heightened HDCC tensile ductility, while greater harmless porosity is associated with elevated initial crack strength and fracture toughness, albeit at the expense of reduced tensile ductility. Higher plastic viscosity (0.21 Pas similar to 2.38 Pas) and lower yield stress (1.24 Pa similar to 15.35 Pa) increase harmful pore formation, reducing matrix fracture toughness but enhancing HDCC tensile ductility. Considering both fiber dispersion and pore structure alterations is crucial in HDCC design. Under specified conditions, adjusted rheological parameters yield HDCC with over 40% harmful pores, over 90% fiber dispersion, compressive strength up to 30 MPa, and 5% ductility, with crack widths below 100 mu m and an average spacing of 2.37 mm, indicating multislit cracking close to saturation. These findings provide valuable insights for HDCC ratio design.