Carbon Effect on Tensile and Wear Behaviors for a Dual-Phase Fe61.5 Cr17.5ni13al8 Alloy

Muhammad Azeemullah,Q. P. Cao,X. D. Wang,S. Q. Ding,M. Abubaker,D. X. Zhang,J. Z. Jiang

DOI: https://doi.org/10.1016/j.msea.2024.147128

2024-01-01

Abstract:High entropy alloys (HEAs) series were produced by doping carbon into Fe61.5Cr17.5Ni13-xAl8Cx (x = 0, 0.25, 0.5, and 1.5 at.%) by a vacuum arc melting. The carbon doping effect on the phase composition, mechanical properties, and wear behavior was studied. Fe61.5Cr17.5Ni13Al8 alloy microstructure was a heterogeneous structure comprising FCC, BCC, and B2 phases. By introducing carbon into Fe61.5Cr17.5Ni13-xAl8Cx (x = 0, 0.25, 0.5, and 1.5 at.%), the BCC phase fraction increased with decreasing FCC phase during annealing, accompanied by the formation of M23C6-like carbides at temperatures of 800 degrees C and 900 degrees C. The carbon-doped HEAs exhibited enhanced mechanical properties compared to the carbon-free HEAs, including higher tensile strength (1580 MPa), notable ductility (similar to 20 %), reduced friction coefficient (0.50), and improved wear resistance. Among the carbon-doped HEAs, the HEA with x = 0.5 at.% and annealed at 800 degrees C demonstrated exceptional wear resistance due to the compensations of attaining a balance between strength and elasticity.