Abstract:The effect of rolling temperature on the incomplete recrystallization behavior and the relationship to mechanical properties in 0.06C–4Mn-1.2Cr (wt.%) steel was investigated. Three plates of experimental steel were produced by hot rolling at different temperatures and intercritical annealing processes in this study. The microstructure of experimental steels was examined by optical microscopy (OM), scanning electron microscopy (SEM), X-ray diffraction (XRD), electron backscatter diffraction (EBSD), and transmission electron microscope (TEM). The mechanical properties of test steel were examined by impact test and tensile test. Austenite reversion and cementite precipitation-dissolution was numerically simulated under the assumption of local equilibrium. With the decrease of hot rolling temperature from 1000 °C to 800 °C, the uniform equiaxed prior austenite grains microstructures changed to heterogeneous microstructures of laminated and ultrafine prior austenite grains arranged alternatively. The tensile and impact tests revealed that the medium manganese steels rolling at 800 °C had an excellent combination of mechanical properties. Elongation had a great relationship with retained austenite fraction and stability. The fractography of impact specimens was examined to explore the toughening mechanism of the micro-laminated steels. The steel with uniform equiaxed grain structure exhibited a relatively low tensile strength of 750 MPa and low elongation of ∼20% and an extremely poor low-temperature toughness of ∼40 J at −40 °C. An enhanced low-temperature toughness (∼233 J at −40 °C), as well as an improved tensile strength (823 MPa) and higher elongation of ∼40%, was obtained in the steel with heterogeneous microstructures. The content of austenite in heterogeneous microstructure is twice that in uniform equiaxed grain structure. And cementite dissolved more thoroughly in the heterogeneous microstructure. The high austenite content of heterogeneous microstructures enabled the steel to be significantly stronger and ductile, which contributed to the high tensile strength and elongation to some extent. It is concluded that the effect of interface decohesion resulted in the occurrence of delamination. And the high austenite content and delamination greatly improved the low-temperature toughness of experimental steel.

Effect of Controlled Rolling on the Strength and Toughness of Low‐Alloy Martensitic Steel

The Influence of Warm Rolling Reduction on Microstructure Evolution, Tensile Deformation Mechanism and Mechanical Properties of an Fe-30Mn-4Si-2Al TRIP/TWIP Steel

Effect of hot/warm rolling on the microstructures and mechanical properties of medium-Mn steels

Enhanced mechanical properties of a high-carbon martensite steel processed by heavy warm rolling and tempering

Strengthen and Toughen the Low‐Alloyed Steel by Direct Tempforming

Preparation and Mechanical Behavior of Ultra-High Strength Low-Carbon Steel

Achieving 1.7 GPa Considerable Ductility High-Strength Low-Alloy Steel Using Hot-Rolling and Tempering Processes

Tailoring retained austenite and mechanical property improvement in Al–Si–V containing medium Mn steel via direct intercritical rolling

Effect of rolling temperature on microstructure and mechanical properties of medium manganese steel

Low-Carbon Bainite Steel with High Strength and Toughness Processed by Recrystallization Controlled Rolling and Ultra Fast Cooling (RCR+UFC)

Microstructure and Mechanical Properties of a Novel Cold Rolled Medium-Mn Steel with Superior Strength and Ductility

High strength-toughness combination of a low-carbon medium-manganese steel plate with laminated microstructure and retained austenite

An original way for producing a 2.5 GPa strength ductile steel by rolling of martensite

Influence of warm rolling temperature on multi-scale lamellar structure and mechanical properties of medium carbon steel

Achieving ultrahigh strength by tuning the hierarchical structure of low-carbon martensitic steel

Advancement of strength and toughness in ultra-low carbon martensitic stainless steel by reversed austenite

New observations of the twinning effect and austenite stability in intercritical quenched and tempered steel with high strength

Overcoming the strength-ductility trade-off in metastable dual-phase heterogeneous structures using variable temperature rolling and annealing

Achieving Well‐Balanced Strength and Ductility in Warm‐Rolled Fe–30.5Mn–8Al–1.0C Lightweight Austenitic Steels via Aging Treatment

Strength‐Ductility Synergy in an Austenitic Stainless Steel Processed by Warm Rolling and Subsequent Cryogenic Treatment

The Low‐Temperature Toughness Improvement of High‐Strength Low‐Alloy Steel Due to the Microstructural Changes Caused by the Reheating/Rolling Temperature