Abstract:In recent years, the increasing potential for the use of high temperature self-lubricating composites as sliding components at extreme environments have attracted great attention on these materials. In the present work, NiCr–BaCr2O4 self-lubricating composites have been prepared using the hot pressing method. The friction and wear properties of NiCr–BaCr2O4 composites were investigated by using a ball-on-disk friction and wear tester in sliding against alumina ball up to 800°C. At room temperature, the NiCr–20BaCr2O4 composite has a friction coefficient of 0.72, which is clearly higher than that (0.44) of NiCr alloy. However, the composites incorporated with BaCr2O4 exhibit distinct improvements in effectively reducing friction and wear in a temperature range of 400–800°C as contrasted with unmodified NiCr alloy. At 800°C, the NiCr–20BaCr2O4 composite exhibits a friction coefficient of 0.27 and a wear rate of 4.5×10–6mm3/(Nm), while the unmodified NiCr alloy has a friction coefficient of 0.41 and a wear rate of 9.2×10–5mm3/(Nm), respectively. At elevated temperatures, a dense and protective oxide glaze layer is generated on the worn surface of composites. The glaze layer was then investigated by means of scanning electron microscopy, laser Raman spectroscopy and nano-indentation. Tribo-oxidation reaction of BaCr2O4 during high temperature wear tests is responsible for the formation of the protective glaze layer. The newly formed BaCrO4 contains lubricious hexavalent-Cr6+, which can promote the densification of oxide glaze layer, and finally generate a dense lubricating film to effectively reduce friction and wear at elevated temperatures.

Ultralow Friction and Low Wear Behavior of In-Situ Formed NiTiO3 from 60niti Alloy at 350 °C

Friction and wear performance of a NiAl-8 wt% serpentine-2 wt%TiC composite at high temperatures

Effect of Temperature on the Friction and Wear Behaviors of Cr3C2–20 Wt% Ni Cermets

Friction and Wear Properties of Ni3Si Alloy with Ti Addition at High Temperatures

Wear Properties of NiAl Based Materials

High-temperature compressive properties and tribological behaviour of Mo2NiB2–Ni cermets

Effects of temperature on tribological properties of nanostructured and conventional Al2O3–3 wt.% TiO2 coatings

Unlubricated Friction and Wear Behaviors of Al2O3/TiC Ceramic Cutting Tool Materials from High Temperature Tribological Tests

Fabrication and High-Temperature Tribological Properties of Self-Lubricating NiCr–BaMoO 4 Composites

Tribological properties of self-healing NiCrAlY/Cr3C2-Ti3AlC2 coating at high temperatures

Preparation of Self-Lubricating NiTi Alloy and Its Self-Adaptive Behavior

Friction-Induced Hardening Behaviors and Tribological Properties of 60niti Alloy Lubricated by Lithium Grease Containing Nano-BN and MoS2

High temperature and room temperature tribological behaviors of in-situ carbides reinforced Ni-based composites by reactive sintering Ni and Ti2AlC precursor

Sliding Wear Behaviors of the AlNiTi Amorphous Coatings: Effect of Temperatures

Study on High-Temperature, Ultra-Low Wear Behaviors of Ti6Al4V Alloy with Thermal Oxidation Treatment

Improving the mechanical and tribological properties of TiAlSiN coatings by annealing

Study of the high-temperature mechanical properties of Al-6061/NiTi reinforced metal matrix composites

Wear Behavior of TiN/TiAlSiN Nanocomposite Multilayer Coatings from Ambient Temperature to Medium Temperature

Dry Friction and Wear Properties of Silicon Carbide with Nickel and Titanium as Compositions

Friction and Wear Properties of Hot-Pressed NiCr–BaCr2O4 High Temperature Self-Lubricating Composites

Microstructure and Tribological Properties of Reactive Hot Pressed TiN–TiB2 Composites Incorporated with or Without MoSi2 from Room Temperature to 800°C