Abstract:The main problem in the rebar case is corrosion, which is caused by the penetration and diffusion of chloride ions into reinforced concrete structures; therefore, it is essential to give the most attention to preventing or limiting the impact of this condition. So, in order to find a practical solution to the problem of corrosion of rebar, the current article focuses on demonstrating the beneficial effects of green and calcium nitrate inhibitors on chloride-induced corrosion. Thus, this paper presented an analytical procedure based on corrosion rates and the economic cost to evaluate the efficacy of such an inhibitor. Ten samples with various concrete mixtures were divided into two groups according to the type of plasticizer and inhibitor have been immersed in an aqueous solution of 3.5 wt. % sodium chloride at room temperature for 18 months. The optimal results in which the corrosion rate was significantly reduced were for the two groups of concrete mixtures, first group was (C2) which contains 3 wt.% orange peels extract inhibitor mixed with 2.4wt.% Oxydtron as water-resisting admixture, and second group was (E2) included 3 wt.% calcium nitrate inhibitor with 2.4wt.% Oxydtron as water-resisting admixture. These two groups samples have been showed more excellent corrosion resistance against the saline solution after the completed immersion period. The inhibition efficiency analysis showed that there is a direct relationship between the inhibitor concentration and the efficiency of corrosion inhibition. However, the inhibition efficiency in case of samples containing calcium nitrate inhibitor was higher than their counterparts containing green inhibitor extract. Finally, the economic cost analysis showed that, the cost of the green inhibitor extract-containing samples was lower than that of the calcium nitrate inhibitor-containing samples.

A Novel LDHs-VB3- Inhibitor for Rebar Corrosion in Simulated Concrete Pore Solution: Synthesis, Performance and Mechanism

Developing a Novel Expression for Chloride Ion Concentration Threshold in Reinforced Concrete: Integration of Electrochemical Analysis and Time-Dependent Modeling

The Electrochemical Characterization of Rebar Passivation Film in Simulated Concrete Media

Corrosion Inhibition and Adsorption Behavior of (3-Aminopropyl)-triethoxysilane on Steel Surface in the Simulated Concrete Pore Solution Contaminated with Chloride

Bidirectional Electromigration of A Corrosion Inhibitor in Chloride Contaminated Concrete

Ammonium Phosphate as Inhibitor to Mitigate the Corrosion of Steel Rebar in Chloride Contaminated Concrete Pore Solution

Anticorrosion Performance and Field Application of a New Rebar Inhibitor

Effect of Chloride Ions Concentrations to Breakdown the Passive Film on Rebar Surface Exposed to L-Arginine Containing Pore Solution

Merged CMOS/bipolar technologies and microwave MESFETs utilizing zone-melting-recrystallized SOI films

Analysis of corrosion rate, inhibition efficiency, and economic cost of XD3 reinforced concrete related to inhibitor and plasticiser types

Smart Inhibition Action of Amino Acid-Modified Layered Double Hydroxide and Its Application on Carbon Steel

Unveiling the corrosion inhibition mechanisms of Anion-Mediated LDH nanopores on water and ion transport by molecular dynamics simulations

Effectiveness of an amine-based inhibitor—guanidine for steel in chloride-contaminated concrete

Three-phase Modelling of Electrochemical Chloride Removal from Corroded Steel-Reinforced Concrete

Chloride-induced Corrosion Patterns of Reinforcements in Simulated Pore Solutions of Calcium Sulfoaluminate Cement Concrete: an Analytical Study

Sodium Succinate as a Corrosion Inhibitor for Carbon Steel Rebars in Simulated Concrete Pore Solution

Effect of Imidazoline Inhibitor on the Rehabilitation of Reinforced Concrete with Electromigration Method

CaFe-Based Layered Double Oxides With Superior Iron Alloy Corrosion Inhibition Behaviors in Aggressive Seawater Environment

Experimental study on electrical characteristics of ions in concrete at early age under electric field

Effect of the stirrup on the transport of chloride ions during electrochemical chloride removal in concrete structures

Inhibiting property of nitrite intercalated layered double hydroxide for steel reinforcement in contaminated concrete condition