Abstract:By tuning the intrinsic feature of a Natrium super ionic conductor (NASICON) NASICON‐type solid electrolyte via calcium ion (Ca2+) doping to fulfill record‐low interfacial resistances of 0.4 Ω cm2 at 45 °C and 110 Ω cm2 at −20 °C, a rechargeable solid‐state Na‐metal battery operating in a wide temperature range from −20 to 45 °C to promote the concept of all‐season applicable solid‐state batteries is achieved. Achieving satisfactory performance for a solid‐state Na‐metal battery (SSNMB) with an inorganic solid electrolyte (SE), especially under freezing temperatures, poses a challenge for stabilizing a Na‐metal anode. Herein, this challenge is addressed by utilizing a Natrium super ionic conductor (NASICON) NASICON‐type solid electrolyte, enabling the operation of a rechargeable SSNMB over a wide temperature range from −20 to 45 °C. The interfacial resistance at the Na metal/SE interface is only 0.4 Ω cm2 at 45 °C and remains below 110 Ω cm2 even at −20 °C. Remarkably, long‐term Na‐metal plating/stripping cycles lasting over 2000 h at −20 °C are achieved with minimal polarization voltages at 0.1 mA cm−2. Further analysis reveals the formation of a uniform Na3−xCaxPO4 interphase layer at the interface, which significantly contributes to the exceptional interfacial performance observed. By employing a Na3V1.5Al0.5(PO4)3 cathode, the full battery system demonstrates excellent adaptability to low temperatures, exhibiting a capacity of 80 mA h g−1 at −20 °C over 50 cycles and retaining a capacity of 108 mAh g−1 (88.5% of the capacity at 45 °C) at 0 °C over 275 cycles. This research significantly reduces the temperature threshold for SSNMB operation and paves the way toward solid‐state batteries suitable for all‐season applications.

A 110 Wh kg−1 Ah-level anode-free sodium battery at −40°C

A High‐Power Rechargeable Sodium‐Ion Full Battery Operating at −40 °C

A Free-Sealed High-Voltage Aqueous Polymeric Sodium Battery Enabling Operation at −25°C

Low-temperature and high-rate sodium metal batteries enabled by electrolyte chemistry

Aggregate-Dominated Dilute Electrolytes with Low-Temperature-Resistant Ion-Conducting Channels for Highly Reversible Na Plating/Stripping

Regulating Ion‐Dipole Interactions in Weakly Solvating Electrolyte towards Ultra‐Low Temperature Sodium‐Ion Batteries

Extending the low-temperature operation of sodium metal batteries combining linear and cyclic ether-based electrolyte solutions

An Anti-Freezing Pure Inorganic Electrolyte for Long Cycle Life Aqueous Sodium-Ion Batteries at -40 °C

A Quasi‐Solid‐State Polyether Electrolyte for Low‐Temperature Sodium Metal Batteries

An Ultrastable Low-Temperature Na Metal Battery Enabled by Synergy between Weakly Solvating Solvents.

A high-voltage anode-free rechargeable sodium battery.

Low‐Temperature Sodium–Sulfur Batteries Enabled by Ionic Liquid in Localized High Concentration Electrolytes

Cost attractive hydrogel electrolyte for low temperature aqueous sodium ion batteries

A Multifunctional Interphase Layer Enabling Superior Sodium-Metal Batteries under Ambient Temperature And-40 °C

Low‐Temperature and Fast‐Charge Sodium Metal Batteries

Rechargeable Solid‐State Na‐Metal Battery Operating at −20 °C

Multifunctional Interphase Layer Enabling Superior Sodium Metal Battery under Ambient Temperature and ‐40 °C

Bendable quasi-solid-state aqueous sodium-ion batteries operated at -30 °C

High-voltage Aqueous Planar Symmetric Sodium Ion Micro-Batteries with Superior Performance at Low-Temperature of −40 ºc

Aqueous Batteries Operated at -50 °C

High-voltage aqueous planar symmetric sodium ion micro-batteries with superior performance at low-temperature of −40 oC