High-temperature Relaxation Promoting Form II-to-form I Phase Transition of Polybutene-1

Yu Han,Xiangyang Li,Tangguo Liu,Jianjun Ding,Yongxing Lin,Lin Chen,Ningdong Huang,Feng Wang,Xingyou Tian

DOI: https://doi.org/10.1016/j.polymer.2024.126893

IF: 4.6

2024-01-01

Polymer

Abstract:Amorphous coils between crystalline layers of polybutene-1, especially intercrystalline links within, were thought to play a critical role in form I nucleation, but recent experiments found that it actually played a negative role in form II to form I phase transition, that is, obstructing form I growth by hindering translational movements of form II stems. To reexamine the role of amorphous coils, a high molecular weight PB-1 sample was annealed at a high temperature ranging from 40 to100 oC after low-temperature nucleation. Results indicated that high-temperature annealing after low-temperature nucleation facilitated disentanglement of amorphous coils, promoting subsequent form I growth. The growth rate of form I doubled after relaxation at 100 oC for 5 min. We also explored nucleation mechanism of form I by moving the relaxation process before nucleation of form I. Results indicated that the form I nuclei were highly fragile crystals on the ends of form II lamellae, suggesting critical role of internal stress in form I nucleation. With this study, we assume that the role of amorphous coils in form II to form I phase transition is indispensable. The seemingly conflicting roles of amorphous coils in form I nucleation and growth can be relieved partly by addition of a high-temperature relaxation process. We suggest addition of a high-temperature relaxation process between nucleation and growth to further expedite phase transition in a high molecular weight PB-1 sample. This study is beneficial to further understand form II to form I phase transition.