Abstract:Galvanizing is the process of applying a protective zinc or zinc alloy coating to steel or iron which acts as a sacrificial anode to protect the underlying steel or iron. These coatings are mainly used in the automotive and construction industry where corrosive environments will be encountered. There has been a drive to improve the performance of galvanised coatings through alloy additions, initially Al (5 – 55 wt%) and more recently through the development of Zn - Al - Mg coatings. Here, Al and Mg are added as minority additions (typically 1 - 3 wt %) to improve corrosion resistance allowing thinner coatings to be used thus saving material, weight and cost. The assessment of the corrosion performance of such coatings is often evaluated through standardised tests. An industry standard test known as Prohesion or ASTM G85 Annex A5 is carried out on metallic coatings as it is thought to better represent long-term natural exposure than a regular salt spray test. The Prohesion test is a cyclic accelerated corrosion test using an electrolyte of 0.4% Ammonia sulphate and 0.05% sodium chloride (NaCl). This investigation aims to determine the effects on the corrosion performance of zinc-aluminium alloys and zinc-aluminium-magnesium alloys of varying compositions immersed in Prohesion solution. Previous work on this topic suggests that magnesium containing alloys were particularly susceptible to accelerated corrosion in Prohesion solution. Here, several zinc based alloys were immersed in Prohesion solution as well as a control 0.45% sodium chloride solution and subjected to electrochemical testing. The electrochemical techniques used to test said substrates are linear polarisation resistance (LPR), scanning vibrating electrode technique (SVET) and time-lapse optical microscopy (TLM) all for 24 hours. The alloys that underwent testing are shown in Table 1. Table 1: Table showing the composition of substrates used. Sample number Composition 1 Zn-<0.2wt%Al 2 Zn-5wt%Al 3 Zn-55wt%Al 4 Zn-1.2wt%Al-Zn1.2wt%Mg 5 Zn-3.5wt%Al-3wt%Mg 6 Zn-6wt%Al-3wt%Mg The results from the TLM showed differences in the corrosion mechanism that is dependent on the alloy composition and electrolyte. Generally, all substrates immersed in the control 0.45% NaCl showed localised corrosion with distinct anodes developing surrounded by a ring of corrosion product and white rust is observed on the surface of the substrate. The initial site of anodic attack in the microstructure was dependent on the alloy composition. However, when immersed in the Prohesion solution significant differences were observed dependent on the alloy composition. For Zn-Al-Mg coatings rapid attack of zinc-magnesium phases was observed especially in the eutectic regions followed by aggressive attack of the entire exposed surface of the alloy within 6 hours. Additionally, no corrosion product rings formed. For Zn-Al alloy coatings, the zinc phases were preferentially attacked with the aluminium containing phases appearing to be resistant to corrosion during the duration of the tests. No white rust was seen on the surface of the substrates and instead a dark surface/corrosion product film was observed. The corrosion rate from the LPR data measured at hourly intervals over 24 hours increases when substrates are immersed in Prohesion solution compared to NaCl, with the most noticeable increase seen when there are zinc-magnesium phases present within the alloy. The largest increase in corrosion rate mm per year (mmpy) was seen in sample 5 with it increasing from 0.15 mmpy after 24 hours in the control solution to 0.55 mmpy in the Prohesion solution after 24 hours. The same is observed with the SVET results showing that the ammonium ions are having a significant damaging effect on the Zn-Al-Mg metallic coatings. The proposed corrosion mechanism for Zn-Al-Mg alloy coatings in Prohesion solution is preferential dissolution of MgZn 2 in eutectic phases due to reactivity of Mg producing Mg(OH) 2 which is a highly basic hydroxide. Due to the basic nature of Mg(OH) 2 , Ammonium (NH 4 + ) cations react with Mg(OH) 2 producing Mg 2+ and Ammo -Abstract Truncated-

Influence of Magnesium Chloride on the Electrodeposition of Zinc from the 1,3-Dimethyl-2-imidazolidinone/zncl2 System

The Effect of Suspended Particles on the Corrosion Resistance of Electrodeposited Zinc Powders

Physicochemical properties of 1,3-dimethyl-2-imidazolinone−ZnCl2 solvated ionic liquid and its application in zinc electrodeposition

Regulating Zn-ion Solvation Structure and Zn(002) Deposition for Stable Zn Anode

Theoretical and experimental studies on the electrodeposition of magnesium in 1,3-dimethyl-2-imidazolidinone organic solvent at room temperature

Electrolytic Etching of AZ91D Mg Alloy in AlCl3–EMIC Ionic Liquid for the Electrodeposition of Adhesive Al Coating

Rapid Electrodeposition and Corrosion Behavior of Zn Coating from a Designed Deep Eutectic Solvent

Influence of Electrolyte Choice on Zinc Electrodeposition

Effect of Chloride Ions on the Electrochemical Performance of Magnesium Metal‐Organic‐Frameworks‐based Semi‐Solid Electrolytes.

Ternary alloying additions and multilayering as strategies to enhance the galvanic protection ability of Al-Zn coatings electrodeposited from ionic liquid solution

Effect of Mg on the Corrosion Resistance of Hot-Dip Zn-Cu-Ti Alloy

Study of Electroless-Deposited Zn on the Surface of Mg-Li Alloy

Regulating Zn2+ Solvation Shell Through Charge‐Concentrated Anions for High Zn Plating/Stripping Coulombic Efficiency

Thermodynamic and Kinetic Properties of Mg(II) in LiCl-KCl Melt and the Formation of Zn-Mg Alloy on Liquid Zn Electrode

Effect of Zinc Immersion Pretreatment on the Electro-Deposition of Ni Onto AZ91D Magnesium Alloy

Effect of EDTA and NH 4 Cl additives on electrodeposition of Zn–Ni films from choline chloride-based ionic liquid

Influence of Concentration of Zinc Ions on Electrocrystallization Process of Zinc

Biological action of leptin as an angiogenic factor.

Electrodeposition of aluminum–magnesium alloys from an aluminum-containing solvate ionic liquid at room temperature

Eco-Friendly Electrodeposition of Al-Zn Alloy from AlCl3-Urea Deep Eutectic Solvent

The Effect of Ammonium Ions on the Corrosion Resistance of Zinc - Aluminium and Zinc - Aluminium - Magnesium Coated Steel