Up- and Down-Conversion Photoluminescence Properties of Ho2O3 Doped YbAG Single Crystals Prepared by Optical Floating Zone Method

Ninghan Zeng,Shoulei Xu,Huiting Zhang,Wenxia Wu,Zhonghua Zhu,Yazhao Wang,Peng Zhang,Limin Wu,Bernard Albert Goodman,Wen Deng

DOI: https://doi.org/10.1016/j.ceramint.2024.01.394

IF: 5.532

2024-01-01

Ceramics International

Abstract:Single crystals of garnets with composition Yb 2.96- x Y x Ho 0.04 Al 5 O 12 ( x = 0, 2.92, 2.96) were grown by optical floating zone method, and shown by XRD measurements to be in the cubic phase. EDS spectra show that Ho 3 + and Yb 3 + were homogenously distributed in the structure. As shown by the transmission and absorption spectra, the Yb 2.96-x Y x Ho 0.04 Al 5 O 12 crystals are highly transparent and can function as excellent optical crystals. Compared to the Y 2.96 Ho 0.04 Al 5 O 12 crystal, the Yb 2.96 Ho 0.04 Al 5 O 12 crystal has an additional strong broad absorption in the 836 - 1070 nm range, which increases its absorption of 980 nm photons. The optical band gaps of the Yb 2.96- x Y x Ho 0.04 Al 5 O 12 crystals decrease with increasing Yb 2 O 3 concentration. Furthermore, differences with Yb 2 O 3 concentrations in the Yb 2.96- x Y x Ho 0.04 Al 5 O 12 crystals were observed for the first time in the up- and downconversion photoluminescence. Under excitation with a 980 nm laser, the up -conversion PL spectra of the Yb 2.96- x Y x Ho 0.04 Al 5 O 12 crystals show several emission peaks at 548 nm, 665 nm and 775 nm, and their intensities increase with Yb 2 O 3 concentrations. In the Yb 2.96 Ho 0.04 Al 5 O 12 crystal, Yb 3 + not only is a component of the garnet structure, but it also acts as a sensitizer. In regards of down -conversion, under excitation at 454 nm, the downconversion PL spectra of the Yb 2.96- x Y x Ho 0.04 Al 5 O 12 crystals show strong emission peaks at 550 nm, and their intensities decrease with increasing Yb 2 O 3 concentrations, which is considered to be the consequence of increasing matrix density.