Study on Visible and Infrared Luminescence Properties of Y2O2S∶Ho3+,Yb3+ Nanocrystals under 980 Nm Excitation
ZHANG Nan,FU Yao,LUO Xi-xian,XING Ming-ming
DOI: https://doi.org/10.3969/j.issn.1001-9731.2014.12.016
2014-01-01
Abstract:Near-spherical Y2 O2 S∶Ho3+,Yb3+ nanocrystals (NCs)were prepared by coprecipitation method fol-lowed by a solid-gas sulfuration technic.The nanocrystals are in hexagonal structure,and the particle size was 40 nm on average.Under the excitation of 980 nm laser diode (LD),more systematic researches on lumines-cence properties of Y2 O2 S∶Ho3+,Yb3+ NCs in a broad range from 450 nm to 1 500 nm have been performed. According to the luminescence measurement results,three different emissions located at 545,655,1 180nm can be observed,which are derived from 5 F4/5 S2→5 I8 ,5 F5→5 I8 ,5 I6→5 I8 transitions,respectively.The upconver-sion luminescence (UCL)efficiency of Ho3+ in the nanocrystals can be improved obviously by co-doping Yb3+. However,because of the high-energy vibration quantum produced by surface adsorption,the 5 F4/5 S2→5 F5 and 5 I6→5 I7 multi-phonon relaxations of Ho3+ are very efficient,and the red emission could be held up hardly.In addition,the increasing content of Yb3+(no more than 6 mol%)can not only improve the population of 5 F4/5 S2 and 5 I6 energy levels,but also restrain the 5 I6→5 I7 multi-phonon relaxation in a certain degree,which results in an enhancement on green and infrared (IR)emissions,but a decrease on red emission.Nevertheless,the inten-sity ratio of green to red emission (IG/IR)obtained in Y2O2S∶Ho3+,Yb3+ NCs was only 3.75,which was much smaller than that of micron Y2O2S (46.6).This was because of another possible populating process (5 F4/5 S2→5 F5 )of 5 F5 energy level.When Yb3+ content was higher than 6 mol%,(5 F4/5 S2 ,2 F7/2 )→(5 I6 ,2 F5/2 ) inverse energy transmission make the green and red emission intensities decrease sharply,but this process was beneficial to the population of 5 I6 energy level and leads to an enhancement on IR emission intensity.These changes weakens the I G/I R ratio,and give rise to a remarkablely increase on I IR/I R .