Study on visible and infrared luminescence properties of Y;O;S:Ho;,Yb; nanocrystals under 980 nm excitation

zhang nan,fu yao,luo xixian,xing mingming

2014-01-01

Abstract:Near-spherical Y2O2S∶Ho3+,Yb3+ nanocrystals(NCs)were prepared by coprecipitation method followed by a solid-gas sulfuration technic.The nanocrystals are in hexagonal structure,and the particle size was 40nm on average.Under the excitation of 980nm laser diode(LD),more systematic researches on luminescence properties of Y2O2S∶Ho3+,Yb3+ NCs in a broad range from 450nm to 1 500nm have been performed.According to the luminescence measurement results,three different emissions located at 545,655,1 180nm can be observed,which are derived from5F4/5S2→5I8,5F5→5I8,5I6→5I8 transitions,respectively.The upconversion luminescence(UCL)efficiency of Ho3+in the nanocrystals can be improved obviously by co-doping Yb3+.However,because of the high-energy vibration quantum produced by surface adsorption,the 5F4/5S2→5F5 and 5I6→5I7 multi-phonon relaxations of Ho3+are very efficient,and the red emission could be held up hardly.In addition,the increasing content of Yb3+(no more than 6mol%)can not only improve the population of 5F4/5S2and 5I6energy levels,but also restrain the 5I6→5I7 multi-phonon relaxation in a certain degree,which results in an enhancement on green and infrared(IR)emissions,but a decrease on red emission.Nevertheless,the intensity ratio of green to red emission(IG/IR)obtained in Y2O2S∶Ho3+,Yb3+ NCs was only 3.75,which was much smaller than that of micron Y2O2S(46.6).This was because of another possible populating process(5F4/5S2→5F5) of 5F5 energy level.When Yb3+ content was higher than 6mol%,(5F4/5S2,2F7/2)→(5I6,2F5/2)inverse energy transmission make the green and red emission intensities decrease sharply,but this process was beneficial to the population of 5I6 energy level and leads to an enhancement on IR emission intensity.These changes weakens the IG/IRratio,and give rise to a remarkablely increase on IIR/IR.