Synthesis and Thermal Properties of Myristic Acid/Nano-TiO2/Carbon Additives Composite Phase Change Materials
Tingwei Fu,Wenze Wang,Guiyin Fang
DOI: https://doi.org/10.1007/s10765-024-03346-y
2024-03-04
International Journal of Thermophysics
Abstract:A novel composite phase change material, myristic acid (MA)/nano-titanium dioxide (nano-TiO 2 )/carbon additives, was synthesized via a melt blending method, in which MA serves as phase change material, nano-TiO 2 acts as support material, and carbon additives are used as thermally conductive enhancer. A series of leakage tests have shown that MA/nano-TiO 2 can maintain shape stability during the phase transition when the content of MA in MA/nano-TiO 2 does not exceed 50 %. The FT-IR and XRD results demonstrated that there is no chemical reaction among the various components of the MA/nano-TiO 2 /carbon additive. When the content of MA is 50 %, the melting temperature of MA/nano-TiO 2 /carbon additives is about 54 °C and the melting enthalpy is about 80 J·g −1 . When the content of all three carbon additives, multiwall carbon nanotubes, graphene, and expanded graphite, is 2.5 %, the corresponding thermal conductivity of MA/nano-TiO 2 /carbon additives is 0.532 W/(m·K), 1.128 W/(m·K), and 1.382 W/(m·K), respectively. The thermal conductivity of these three types of MA/nano-TiO 2 /additives is 1.23, 2.62, and 3.21 times that of MA/TiO 2 , respectively. Moreover, the decomposition temperature of these three types MA/nano-TiO 2 /carbon additives composites is around 245 °C. Therefore, the working ambient temperature of MA/nano-TiO 2 /additive composites should be lower than 245 °C.
thermodynamics,mechanics,chemistry, physical,physics, applied