Corrosion Behavior of Surface Modified Alloy Inconel 625 in Chloride Molten Salts

Siyu Chen,Xian Zhang,Teng Li,Jing Liu,Kaiming Wu

DOI: https://doi.org/10.11933/j.issn.1007-9289.20221121001

2024-01-01

China surface engineering

Abstract:With the implementation of a global sustainable development strategy, further development of solar energy resources has been pushed to commanding heights. Presently, nitrate and carbonate are the main energy storage materials in solar tower power generation systems; however, the application temperature is generally lower than 700 degrees C. The maximum temperature of chloride molten salt can reach 900 degrees C as a heat transfer and heat storage medium, but it causes serious corrosion to metal parts. As a nickel-based superalloy, Inconel 625 has the advantages of high-temperature resistance, corrosion resistance, oxidation resistance, and fatigue resistance. However, there are few studies on the high-temperature corrosion behavior of Inconel 625 in chloride molten salt. In this study, Inconel 625 and the surface modified Inconel 625 (ST In625) after surface mechanical grinding and annealing at 750 degrees Care evaluated. The microstructures and mechanical properties of the two alloys are characterized using backscattered electron diffraction (EBSD) and microtensile tests. The two alloys are immersed in molten binary and ternary chloride salts, and their static corrosion rates are analyzed using the weight loss method. Field emission electron microscopy (SEM / EDS), laser confocal micro-Raman spectrometry (Raman), and field emission electron probe analysis (EPMA) are used to characterize the surface and cross-sectional morphologies, analyze the composition of the corrosion products and evaluate the high-temperature corrosion mechanism of the two alloys in chloride molten salt. The results showed that the grain size of ST In625 obtained after mechanical grinding and annealing was smaller and more uniform than that of In625. Moreover, ST In625 has small-angle grain boundaries with a uniform distribution, and its alloy strength increases significantly, whereas its tensile plasticity decreases. At the initial corrosion stage, Cr2O3 and NiCr2O4 were the main oxide films formed in the molten chloride salt of the two samples, and the corrosion pits on the surface of ST In625 were fewer than those of In625, which was due to the lower corrosion sensitivity and better self-passivation performance of the nano-twin layer on the surface of ST In625. In the later stage of corrosion, NiO was detected on the surface of both samples. No obvious oxide layer was formed on the surface of the two alloys in the binary chloride molten salt, and obvious corrosion pits appeared, whereas new Cr2O3 and NiCr2O4 oxide layers were formed on the surfaces of the two alloys in the ternary chloride molten salt, and no corrosion pits appeared. Therefore, the corrosion loss of ST In625 in the chloride molten salt was small, and the corrosion resistance was significantly improved. The corrosion rates of the two alloys in the binary chloride molten salt were low; however, intergranular corrosion was evident. Moreover, the corrosion rate was high in the ternary chloride molten salt, and the intergranular corrosion was slight. This study improves the corrosion resistance of nickel-based alloys in chloride molten saltenvironments by surface modification and provides a new idea for the selection of metal components for solar thermal power storage materials. In the future, surface modification and heat treatment can improve the corrosion resistance of nickel-based alloys and other high-temperature-resistant metals in molten salt environments, which have the potential for industrial application. The servicebehavior of high-temperature-modified alloys in industrial environments is worthy of further investigation.