Hydrogen-prompted heterogeneous development of dislocation structure in Ni
Qingqing Sun,Jing He,Akihide Nagao,Yong Ni,Shuai Wang
DOI: https://doi.org/10.1016/j.actamat.2022.118660
IF: 9.4
2022-12-28
Acta Materialia
Abstract:First documented in 1875, the deterioration of mechanical properties of hydrogen-containing metals is a long-standing yet unsolved problem in materials science. In this work, the evolution of dislocation structures in different orientated grains (i.e., near [100], [110], and [111]) of the uncharged and hydrogen-charged (400 and 1200 ppm) polycrystalline Ni were systematically investigated by combining electron backscatter diffraction, focused ion beam and scanning transmission electron microscopy. By using site-specific characterization methods, for the first time, we discover that hydrogen-enhanced localized plasticity (HELP) is orientation-dependent, with the following sequence: [100] > [111] > [110]. Massive incompatibility between different orientated grains, induced by the orientation dependence of HELP, contributes to the premature intergranular fracture of Ni, especially for the 400 ppm H-charged Ni. Our results suggest that optimizing orientation distribution is a potential approach for enhancing metals' resistance to hydrogen damage. The relative contribution of HELP and hydrogen-enhanced decohesion (HEDE) mechanisms in hydrogen embrittlement of Ni is also analyzed quantitatively for 400 and 1200 ppm H-charged samples. For 400 ppm H-charged Ni, a strong synergistic interaction exists between HELP and HEDE mechanisms, and the HELP mechanism plays a critical role in premature fracture. While for 1200 ppm H-charged Ni case, HELP effect on final failure is marginal and HEDE is the dominant embrittlement mechanism.
materials science, multidisciplinary,metallurgy & metallurgical engineering