Temperature Field and Microstructure Simulation of Directional Solidification Process of Single Crystal Blade Prepared Efficiently with Different Module Structures

Yang Wenchao,Sa Shipeng,Hao Wenshuo,Qin Jiarun,Zhang Jun,Liu Lin

DOI: https://doi.org/10.12442/j.issn.1002-185X.20220837

2023-01-01

Rare Metal Materials and Engineering

Abstract:For the stray grain problem of 18 single crystal blades in high efficiency preparation due to the non-uniform temperature field, three different module structures with the same production capacity were designed. The high rate solidification of DD6 Ni-based superalloy under different module structures was simulated by ProCast software and CAFE model, and the influence of the temperature field evolution and the withdrawal rate on stray grains was analyzed. The results show that the solid-liquid interface of the single-layer module becomes curved seriously because the cooling efficiency of side close to the center pillar is higher than that of the side close to the furnace body due to weak heat preservation effect of center pillar, and it has a large undercooling and tendency to form stray grains. By adding a sleeve to the single-layer module to increase the heat preservation effect, the temperature field can be changed effectively, and the degree of bending is reduced to avoid the nucleation of stray grain. The double-layer superimposed module has a uniform temperature field and a low undercooling, which can decrease the tendency of stray grain effectively. Both the double-layer superimposed module and the sleeve module can form a complete single crystal when the withdrawal rate is below 100 mu m/s, while the diameter of the double-layer superimposed module reduces to a half of the diameter of the other two modules, which can reduce the requirement for size of furnace body, achieving efficient preparation of single crystal blades.