A TIO N 2 D Protein Supramolecular Nanofilm with Exceptionally Large Area and Emergent Functions
Dehui Wang,Jin Gu,Qian Li,Liangliang Zhang,Peng Yang
2016-01-01
Abstract:DOI: 10.1002/adma.201506476 originally reported by us in previous work,[16] in which lysozyme dissolved in a neutral buffer could undergo a unique phase transition when mixing it with tris(2-carboxyethyl)phosphine (TCEP) buffer at neutral pH. The phrase of “phase transition” has been previously used to describe the solution and aggregation of proteins.[17] The neutral TCEP reducing buffer could effectively break down the disulfide bond to maintain the free thiol group in a system for next-step biochemical reactions on proteins and subsequent site-specific protein immobilization.[18] Accordingly, the lysozyme conformation change occurred after breaking down its disulfide bond by TCEP to induce heterogeneous nucleation and assembly of lysozyme.[16] Herein, we found that such phase transition instantly transferred the assembled lysozymes onto immersed material surface, and a conformal film was coated onto the surface (Figure 1A). The film attachment was precisely immersion-guided, and mere solution-dipped area was covered by the film. This direct assembly of the film onto substrates showed a similarity to natural S-layer proteins that can evolve to form 2D protein lattices on solid supports including silicon wafers, metals, and polymers.[10–12] Instead of direct film deposition at solid/ liquid interface, a free-floating film can be found at the air/ water interface of the phase transition buffer (Figure 1B). The resultant film could stably be existed on the solution surface without extra degradation or re-dissolution, and further readily transferred onto solid surface when the immersed material under the solution meniscus was lifted up to pass through the air/water interface. For a water-sensitive material, the film coating can be performed in a dry condition (Figure 1C). For this aim, a free-floating film was first transferred onto an agarose hydrogel surface. The gel-carried film then stamped on other material surface for ≈1 min to print the film onto the contacted surface. Through pre-defining the hydrogel shape, the film with determined shape was transferred onto a surface by this contact-printing strategy (Figure 1D,E). On the hydrogel stamp surface, a large portion of materials was just water (the solid content of the hydrogel was 1 wt%). Accordingly, the film was thus just weakly attached onto the gel surface, which was similar to a static-floating state on the water surface. Once the film carried by the gel stamp was contacted with a solid dry substrate, the film then readily bonded with the target substrate, thereby achieving a stable film transfer. Actually, a similar transfer-printing technique with the use of hydrogel as a stamp has also been widely used elsewhere.[19] The lateral size of the free-floating film was as large as the solution deposition area on the substrate. This means, a free-floating protein film with continuous size extending to macroscale could be easily produced by simply defining the deposition area on a substrate surface. At the laboratory scale, a film area as large as the 20 in. in diagonal (0.14 m2) could be easily acquired just after the phase Advanced organic and biological thin films offer multiple opportunities in modern materials world, and practical significances have been made in various fields of surface modification, biomaterials, lithography, optics, and electronics.[1–4] In contrast to organic thin films based on limited fossil source, recyclable biopolymers-derived 2D materials such as ribbons, sheets, lattices, membranes, and films by supramolecular assembly of peptides and proteins at the scales from nano to centimeters, have attracted widespread fundamental interests.[5–14] However, a homogeneous macroscopic material at a meter scale or more to truly rival natural object generally having a giant size remains a challenge.[15] Moreover, low assembly efficiency and speed impede scalable production for practical industry use. Our approach is to report a protein-based supramolecular 2D film with ultra-large area (e.g., 20 in. in diagonal), simple and fast preparation process (completed in minutes), tunable micro/nanoscale thickness, diverse functions, and endurable stability. The film is distinctive in its ease of coating on many types of materials of complex shape, colorless and high optical transparency, and low healthcare risks. Without the doping of any other additives, the natural protein, lysozyme was chosen as the single component to easily construct the film in large scale (Figure S1, Supporting Information). Lysozyme, generally recognized as safe material by the U.S. Food and Drug Administration, provides edible material source, and is commercially available at low cost from egg whites, animal, and plant cells. Special equipment, chemical modification on lysozyme or synthesis is not needed to achieve such film, and simple one-step aqueous assembly is sufficient to afford the film in free-floating or solid-supported manner with high efficiency (Movie S1, Supporting Information). The film can be stably adhered onto a variety of substrates to serve as a versatile platform for multiple end-uses including surface grafting, top-down and bottom-up micro/nanofabrications. We first describe the direct film formation on a surface by simply incubating a material surface in a lysozyme phase transition buffer (Figure 1A). The new lysozyme phase transition was