Generation of Nano-pores in Silk Fibroin Films Using Silk Nanoparticles for Full-Thickness Wound Healing

Jian Liu,Ran Huang,Gang Li,David L. Kaplan,Zhaozhu Zheng,Xiaoqin Wang

DOI: https://doi.org/10.1021/acs.biomac.0c01411

2021-01-15

Biomacromolecules

Abstract:Silk fibroin films are used in tissue engineering due to their biocompatibility, optical clarity, and slow biodegradability. However, the relatively smooth surface and low permeability of these systems may limit some applications; thus, here, a method was developed to generate nano-pores in methanol or ethanol-treated silk fibroin films. The first step was to induce the formation of nanoparticles (50–300 nm diam.) in silk fibroin solutions by autoclaving. After drying in air, the films formed were treated to induce silk β-sheet structures, which condense the bulk silk phase and nanoparticles and phase separation and enlarge the space of bulk silk phase and nanoparticles. These films were then extracted with water to allow the condensed nanoparticles to escape, leaving homogeneous nano-pores (50–300 nm) in the silk fibroin matrix. The introduction of nano-pores resulted in enhanced permeability and minimized loss of the mechanical properties of the nano-porous silk fibroin films (NSFs) when compared to the un-autoclaving-treated silk fibroin films. NSFs promoted cell (human fibroblasts) proliferation and oxygen/nutrition perfusion and significantly enhanced the complete skin-thickness wound healing in a rat model, suggesting the potential use in tissue regeneration or as wound dressing biomaterials for clinical applications.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.biomac.0c01411?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.biomac.0c01411</a>.(Figure S1) Morphological and structural analyses of silk nanoparticles in solution and the films, (Figure S2) structural characterization of the NSF and SF after methanol treatment and water wash, and (Figure S3) morphological analysis and cell adhesion on the NSF and SF (<a class="ext-link" href="/doi/suppl/10.1021/acs.biomac.0c01411/suppl_file/bm0c01411_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

polymer science,biochemistry & molecular biology,chemistry, organic