Abstract:The high redox potential of LiMnPO 4 , ∼4.0 vs. (Li + /Li), and its high theoretical capacity of 170 mAh g −1 makes it a promising candidate to replace LiCoO 2 as the cathode in Li-ion batteries. However, it has attracted little attention because of its severe kinetic problems during cycling. Introducing iron into crystalline LiMnPO 4 generates a solid solution of LiFe x Mn 1− x PO 4 and increases kinetics; hence, there is much interest in determining the Fe-to-Mn ratio that will optimize electrochemical performance. To this end, we synthesized a series of nanoporous LiFe x Mn 1− x PO 4 compounds (with x = 0, 0.05, 0.1, 0.15, and 0.2), using an inexpensive solid-state reaction. The electrodes were characterized using X-ray diffraction and energy-dispersive spectroscopy to examine their crystal structure and elemental distribution. Scanning-, tunneling-, and transmission-electron microscopy (viz., SEM, STEM, and TEM) were employed to characterize the micromorphology of these materials; the carbon content was analyzed by thermogravimetric analyses (TGAs). We demonstrate that the electrochemical performance of LiFe x Mn 1− x PO 4 rises continuously with increasing iron content. In situ synchrotron studies during cycling revealed a reversible structural change when lithium is inserted and extracted from the crystal structure. Further, introducing 20% iron (e.g., LiFe 0.2 Mn 0.8 PO 4 ) resulted in a promising capacity (138 mAh g −1 at C/10), comparable to that previously reported for nano-LiMnPO 4 . Keywords Cathode Lithium manganese phosphate Iron substitution Nanoporous Carbon coating 1 Introduction Since the original study of Padhi et al. lithium transition metal phosphate has been considered a promising cathode material for rechargeable lithium-ion batteries [1] . The inexpensive, inherently non-toxic and stable nature of the olivine structure has led to intensive research and development of these materials over the past 10 years. Previous studies have demonstrated impressive rate capabilities in full batteries with a cathode composed of nano-scale LiFePO 4 particles coated with a thin, electronically conductive layer [2,3] . The recent commercialization of LiFePO 4 further highlights its importance as a cathode for lithium batteries. However, because of its relatively low working-potential (LiFePO 4 : 3.5 V (vs. Li + /Li), LiCoO 2 : 3.7–4.1 V (vs. Li + /Li)), batteries made with this material have a lower overall energy density. Currently, much effort is geared towards developing new cathodes exhibiting the positive electrochemical properties of LiFePO 4 along with greater energy density. Here, we investigate the higher voltage LiMnPO 4 (∼4.0 V vs. Li + /Li) as a promising alternative to LiFePO 4 for the cathode in lithium-ion batteries. LiMnPO 4 is isostructural with LiFePO 4 (olivine) and lithium ion diffusion occurs along a one-dimensional path parallel to the c axis. However, LiMnPO 4 performs more poorly than LiFePO 4 in lithium-ion batteries, and the utilization of its theoretical energy density is seldom realized, even under mild operating conditions [4] . The generally accepted reason for the low observed capacity and rate performance in LiMnPO 4 is the high kinetic barrier due to interface mismatch between MnPO 4 and LiMnPO 4 from a Jahn-Teller distortion [5] . Several attempts have been made to improve performance [6–11] : such as lowering particle size, controlling particle shape (synthesizing plate-shaped particles to decrease the diffusion path), decreasing the size of the unit cell by iron substitution, and doping/substitutions to increase the kinetics. Currently, nano-scale, iron-substituted LiMnPO 4 exhibits the best electrochemical performance [1,12] . However, this electrode typically requires more than 25 wt% carbon as the conducting medium, thereby dramatically decreasing the electrodes tap density and increasing cell volume in the full battery. Recent results demonstrated an increase in kinetics when some of the Mn ions were replaced with Fe to form the solid solution LiFe x Mn 1− x PO 4 (e.g., x = 0.1) [12] . Yamada et al. have also shown that this type of substitution increases the electrode capacity, which reaches a maximum close to its theoretical value at x = 0.4 [13] . At very low Fe concentrations ( x ≤ 0.1) a single plateau (3.9 V) is present in the cycling curve, which indicates that the iron may not be contributing much to the capacity since its redox couple occurs at 3.5 V. At higher Fe concentrations ( x > 0.1) both plateaus are clearly visible (3.5 V and 3.9 V). Given the higher potential of the Mn-based phosphate, the energy density is greatest using the least amount of Fe necessary to achieve a high, reversible capacity in the electrode. Currently, the optimal composition of LiFe x Mn 1− x PO 4 is not well defined since it is not known if a near-theoretical capacity can be achieved at lower Fe concentrations. Here we report the performance of carbon-coated nanoporous LiFe x Mn 1− x PO 4 materials at low Fe concentrations ( x = 0, 0.05, 0.1, 0.15, and 0.2). In addition, the nanoporous nature of the material is expected to improve the electrochemical kinetics of the material by increasing its surface area and decreasing the diffusion length of Li + . 2 Experimental We synthesized LiFe x Mn 1− x PO 4 in a conventional solid-state reaction as follows: stoichiometric amounts of lithium carbonate (Li 2 CO 3 ), iron oxalate dihydrogen (FeC 2 O 4 ·2H 2 O), manganese carbonate (MgCO 3 ), ammonium dihydrogen phosphate (NH 4 H 2 PO 4 ), and citric acid (C 6 H 8 O 7 ) were mixed in isopropanol ethanol using a planetary ball mill (Fritsch) for 3.5 days. The precursors obtained from this process were dried, and heat-treated at 300 °C for 2 h and subsequently at 600 °C for 5 h. Powder X-ray diffraction (XRD) patterns were acquired on a Philips XRG 3000 Analytical X-ray Diffractometer to identify the phases present in the as-synthesized material; data were collected from 15° to 65° (2 theta) at 0.6° min −1 . Synchrotron powder diffraction experiments were performed on beamline X7B of the National Synchrotron Light Source (NSLS) at Brookhaven National Laboratory (BNL). The lattice parameters were determined via Rietveld refinements of the synchrotron diffraction data, using an olivine structure with a Pnma space group. Particle morphologies were characterized by scanning electron microscopy (SEM, Hitachi S-4800) and transmission electron microscopy (TEM, JEOL 2100F). Energy dispersive spectroscopy (EDS) was employed in the electron microscopes to determine the distribution of the elements. Thermogravimetric analyses (TGAs) were performed to determine the amount (weight percentage) of residual carbon in the electrode. The electrochemical measurements were made with 2016 coin cells. The electrodes were prepared as follows: the LiFe x Mn 1− x PO 4 ( x = 0, 0.05, 0.1, 0.15, and 0.2) samples were mixed with super-P carbon black, and a binder – polyvinylidene difluoride (PVDF) powder, in the weight ratio of 80:13.5:6.5 and mixed in a solution of N-methyl-2-pyrrolidinone (NMP) to form a slurry. The slurry was then spread onto an aluminum foil, using a doctor blade with a space of 100 μm, and thereafter, dried at 80 °C for 1 h in a vacuum oven to remove the NMP. The coated aluminum foil was calendared and punched into 13 mm diameter discs. The electrodes were dried at 100 °C overnight under vacuum. 1.0 M LiPF 6 in ethylene carbonate and dimethyl carbonate (50:50 in volume) served as the liquid electrolyte, and a sheet of Celgard 2300 was used as the separator. The LiFe x Mn 1− x PO 4 sample constituted the working electrode (cathode), with the lithium metal foil as the counter/reference electrode (anode). The assembled Li/LiFe x Mn 1− x PO 4 cells were cycled between 4.4 and 2.8 V (vs. Li + /Li) at current densities of 15–750 mAh g −1 (assuming 1C = 150 mAh g −1 ) at room temperature. Structural changes occurring in the electrode during the insertion and extraction of the lithium ions were measured by synchrotron XRD using in situ coin cells with a Kapton window. 3 Results and discussion The as-synthesized powder samples were inspected by synchrotron ( Fig. 1 a) and Cu Kα ( Fig. S1 ), XRD to confirm the olivine structure. All samples showed a similar diffraction pattern, except for a slight shift towards higher angles with increasing concentrations of iron. Fig. 1 b shows the changes in the lattice parameters, and the unit-cell volume as a function of iron content. The unit cell shrinks continuously as iron is introduced into the system. The change is approximately linear, but a slight deviation from Vegard's law is observed at low Fe concentrations (<20%), which is similar to previous results [14] . This is likely due to slight deviations in the homogeneity of the material resulting from the solid-state synthesis. These data confirm that all five materials are single-phase olivine compounds, with an orthorhombic structure. The diffraction data also confirm that the LiFe x Mn 1− x PO 4 is a true solid solution of LiMnPO 4 and LiFePO 4 . Synchrotron XRD data, acquired for a more detailed structural analysis, was refined (Rietveld refinement) to determine lattice parameters and atomic positions. LiFe x Mn 1− x PO 4 crystallizes in a Pnma space group (orthorhombic) with lattice constants a = 10.447 Å, b = 6.105 Å, and c = 4.746 Å when x = 0. Therein, the transition metals (Mn and Fe) occupy 4c sites, while Li is in a 4a site. Table 1 compares the cell parameters and Rietveld refinement parameters of LiFe x Mn 1− x PO 4 . Fig. 2 shows the synchrotron powder XRD pattern and the refined pattern from LiMnPO 4 . The morphology of the LiFe x Mn 1− x PO 4 particles was characterized by SEM, high-resolution transmission electron microscopy (HRTEM), and scanning transmission microscopy (STEM). All five samples had a nanoporous structure with particle sizes larger than 1 μm; Fig. 3 shows the SEM images of LiMnPO 4 and LiFe 0.2 Mn 0.8 PO 4 . The more detailed SEM images from LiFe x Mn 1− x PO 4 ( x = 0.05, 0.1, and 0.15) are shown in Supplementary figures (Fig. S2) . To inspect the morphology more closely, we checked the detailed topography with STEM, as shown in Fig. 4 for LiFe 0.2 Mn 0.8 PO 4 . The annular dark-field image reveals a nanoporous morphology with the primary particle sizes ranging from ∼0.5 μm to 2 μm ( Fig. 4 a). Fig. 4 b gives detailed information on the pores on the particles’ surfaces that range from 10 to 100 nm. The nanoporous structure of this material is similar to the material prepared by Dominko et al. [7] . Pore formation is likely from the use of citric acid as the carbon source, and the large quantity of solvent used during grinding. EDS mapping showed that the Fe and Mn ions are uniformly distributed in the particles ( Fig. S3 ). Fig. 5 shows a HRTEM image of a LiFe 0.2 Mn 0.8 PO 4 particle covered by a 3-nm thick carbon film. The crystallites have a well-defined orthorhombic symmetry, and the atomic layer is clearly visible. This figure confirms that the crystal structure is well ordered, suggesting an excellent electrochemical performance in a lithium-ion battery. TGA analysis of the as-prepared powder showed that all five samples have approximately 6 weight percent carbon ( in the supporting information, Fig. S4 ). Small differences in weight loss were observed during the TGAs that were independent of iron concentration. These differences were likely due to variations in the rate of gas flow during sintering, or to slight variations in the amount of carbon used in the precursor. Voltage profiles were measured for LiFe x Mn 1− x PO 4 during galvanostatic discharge at various rates. A single plateau was evident around 4.0 V for x ≤ 0.1, with a second plateau at 3.6 V for samples with iron concentration greater than 10% ( x > 0.1). These 4.0 V and 3.6 V plateaus, respectively, are related to the Mn 3+ /Mn 2+ and the Fe 3+ /Fe 2+ redox couples [15] . Fig. 6 a shows the galvanostatic discharge profiles for LiMnPO 4 at various rates. This sample ( x = 0) had a capacity of about 55 mAh g −1 when it was discharged with a low current (C/15), and exhibited only 20 mAh g −1 at a 2C rate (the C rate was based on a practical capacity of 150 mAh g −1 ). The capacity of the nanoporous LiMnPO 4 was much smaller than that of the nano-scale LiMnPO 4 prepared by Wang et al. [12] . However, we note that less carbon was used in our nanoporous electrodes. In addition, the 4.0 V (vs. Li + /Li) plateau in the voltage, which indicates the redox reaction of Mn 3+ /Mn 2+ , is flat in our results. Iron was incorporated into the material to increase capacity and electrochemical kinetics. At an iron concentration of 15%, the LiFe 0.15 Mn 0.85 PO 4 electrode exhibited a significant enhancement of capacity up to ∼125 mAh g −1 at a rate of C/10 ( Fig. 6 c). At a concentration of 20% iron, the material had a capacity of 130 mAh g −1 at C/10 ( Fig. 6 c). We estimate that the capacity of the active material (not including the carbon) is 133.0 mAh g −1 for LiFe 0.15 Mn 0.85 PO 4, and 138.3 mAh g −1 for LiFe 0.2 Mn 0.8 PO 4 at a rate of C/10. We note that although the capacities achieved with the nanoporous material are similar to those reported for nano-scale LiMnPO 4 [12] , the nanoporous electrodes were prepared by a much simpler solid-state synthesis reaction. In addition, the nanoporous electrodes require roughly 30% less carbon; with a total of ∼18% used (∼4.5% resulting from synthesis and 13.5% added during electrode fabrication) compared with 25% carbon in the nano-scale LiMnPO 4 [8] . It is well known that during the first cycle, the irreversible capacity is partly due to the formation of the surface–electrolyte interphase (SEI) layer [16] . However, the relationship between the structural changes occurring during cycling and loss of capacity is unknown. Hence, it is of interest to detail the changes in the crystal structure (during cycling) and correlate them with the electrochemical performance for the mixed Fe/Mn metal phosphate [15] ; accordingly, we used in situ synchrotron XRD to monitor structural changes in these electrodes during cycling. Fig. 7 a shows the electrochemical cycling curve and corresponding oxidation state (labeled A–J) at which we acquired the synchrotron XRD ( λ = 0.3184 Å) pattern. Fig. S5a shows the XRD pattern between 4° and 20° in 2 θ . The subsequent figures show the same data in more detail over a narrower two-theta range (3–6° ( Fig. 7 b) and from 8° to 12° in 2 θ ( Fig. 7 c)). The (0 2 0) and (1 2 3) peaks decrease when lithium is inserted into the structure, and return to their original state when lithium is extracted. The only noticeable change after the first cycle is in the (1 2 3) peak at 10.4°, which does not reverse to its original intensity and may indicate a re-orientation of the crystals. Overall, there is no major alteration in crystal structure after the first cycle. 4 Conclusion We synthesized nanoporous LiFe x Mn 1− x PO 4 ( x = 0, 0.05, 0.1, 0.15, 0.2) via a simple solid state reaction and characterized the structure, composition and electrochemical properties. The iron-substituted samples formed a solid solution of LiFe x Mn 1− x PO 4 and displayed a decreasing unit-cell volume with increasing iron concentration. In situ XRD demonstrated that the crystal structure underwent a reversible change when lithium was extracted from, or inserted into the material. Characterization of the morphology by SEM, TEM, and STEM verified the nanoporous structure of all our samples. The electrochemical activity of LiFe x Mn 1− x PO 4 may be related to this nanoporous morphology and decreased unit-cell volume. The electrochemical tests revealed that the energy density and rate capability of LiFe x Mn 1− x PO 4 increases with x , while the cell volume of the solid solution simultaneously decreases. Our results demonstrate that when x = 0.2, LiFe x Mn 1− x PO 4 has a capacity of 138.3 mAh g −1 at a rate of C/10. Nanoporous LiFe 0.2 Mn 0.8 PO 4 has an overall energy density comparable to the best performing nano-scale Mn-based phosphates, but can be prepared using an inexpensive solid-state synthesis method. Therefore, we believe nanoporous LiFe 0.2 Mn 0.8 PO 4 is a promising cathode for lithium ion batteries. Acknowledgements The authors thank financial support from the Laboratory Directed Research and Development (LDRD) program under Contract No. DE-AC02-98CH1-886 with the U.S. Department of Energy. The contribution of beamline X7B of National Synchrotron Light Source at Brookhaven National Laboratory is gratefully acknowledged. Appendix A Supplementary data Supplementary data associated with this article can be found, in the online version, at doi:10.1016/j.jpowsour.2010.12.045 . Appendix A Supplementary data References [1] A.K. Padhi K.S. Nanjundaswamy J.B. Goodenough J. Electrochem. Soc. 144 1997 1188 1194 [2] B. Kang G. Ceder Nature 458 2009 190 193 [3] Y.S. Hu Y.G. Guo R. Dominko M. Gaberscek J. Jamnik J. Maier Adv. Mater. 19 2007 1963 1966 [4] M. Yonemura A. Yamada Y. Takei N. Sonoyama R. Kanno J. Electrochem. Soc. 151 2004 A1352 A1356 [5] C.A. Burba R. Frech J. Power Sources 172 2007 870 876 [6] M. Piana B.L. Cushing J.B. Goodenough N. Penazzi Solid State Ionics 175 2004 233 237 [7] R. Dominko M. Bele M. Gaberscek M. Remskar D. Hanzel J.M. Goupil S. Pejovnik J. Jamnik J. Power Sources 153 2006 274 280 [8] N.H. Kwon T. Drezen I. Exnar I. Teerlinck M. Isono M. Graetzel Electrochem. Solid-State Lett. 9 2006 A277 A280 [9] G.Y. Chen J.D. Wilcox T.J. Richardson Electrochem. Solid-State Lett. 11 2008 A190 A194 [10] J.S. Yang J.J. Xu J. Electrochem. Soc. 153 2006 A716 A723 [11] T. Drezen N.H. Kwon P. Bowen I. Teerlinck M. Isono I. Exnar J. Power Sources 174 2007 949 953 [12] D.Y. Wang H. Buqa M. Crouzet G. Deghenghi T. Drezen I. Exnar N.H. Kwon J.H. Miners L. Poletto M. Graetzel J. Power Sources 189 2009 624 628 [13] A. Yamada Y. Kudo K.Y. Liu J. Electrochem. Soc. 148 2001 A747 A754 [14] M. Kopec A. Yamada G. Kobayashi S. Nishimura R. Kanno A. Mauger F. Gendron C.M. Julien J. Power Sources 189 2009 1154 1163 [15] K.W. Nam X.J. Wang W.S. Yoon H. Li X.J. Huang O. Haas J.M. Bai X.Q. Yang Electrochem. Commun. 11 2009 913 916 [16] J.W. Lee M.S. Park B. Anass J.H. Park M.S. Paik S.G. Doo Electrochim. Acta 55 2009 4162 4169

Synthesis and electrochemical properties of Li5 + x Fe1– x Mn x O4 with an antifluorite-type structure as a lithium battery cathode

Ordered LiNi0.5Mn1.5O4 Cathode in Bis(fluorosulfonyl)imide-Based Ionic Liquid Electrolyte: Importance of the Cathode-Electrolyte Interphase

Synthesis and Electrochemical Characteristics of Li₁.₂(Ni₀.₂Mn₀.₆)ₓ(Co₀.₄Mn₀.₄)y(Ni₀.₄Mn₀.₄)₁₋ₓ₋yO₂ (0 ≤ X + Y ≤ 1) Cathode Materials for Lithium Ion Batteries

Insight into fine structures of LiFexMn1-xO2 by synchrotron radiation-based X-ray absorption spectroscopy

Characterization of novel lithium battery cathode materials by spectroscopic methods: the Li5+xFeO₄ system

A Promising Solid‐State Synthesis of LiMn 1‐ y Fe y PO 4 Cathode for Lithium‐ion Batteries

Fe Doped Li1.2Mn0.6-x/2Ni0.2-x/2FexO2 (x≤0.1) As Cathode Materials for Lithium-Ion Batteries

Heavy Fluorination via Ion Exchange Achieves High‐Performance Li–Mn–O–F Layered Cathode for Li‐Ion Batteries

LiFexMn1−xPO4: A cathode for lithium-ion batteries

Synthesis And Characterization Of Novel Cathode Material Li5feo4 For Li-Ion Batteries

Mn-Rich Induced Alteration on Band Gap and Cycling Stability Properties of LiMnxFe1-xPO4 Cathode Materials.

A Cobalt-Free Li(Li0.16Ni0.19Fe0.18Mn0.46)O-2 Cathode for Lithium-Ion Batteries with Anionic Redox Reactions

Enhanced prelithiation performance of Li 5 FeO 4 cathode additive and optimized solid electrolyte interface enabled by Mn substitution

Synthesis and characterization of Li(Li0.23Mn 0.47Fe0.2Ni0.1)O2 cathode material for Li-ion batteries

Structure Evolution from Layered to Spinel during Synthetic Control and Cycling Process of Fe-Containing Li-Rich Cathode Materials for Lithium-Ion Batteries

Electrochemical Performance and in Situ Phase Transition Analysis of Iron-Doped Lithium Manganese Phosphate

Investigation of the Electrochemical Performance and Structural Stability of O6-Type Lithium-Rich Layered Oxide as a Positive Electrode Active Material for Improved Lithium Battery Performance

In-situ Synchrotron X-ray Absorption Studies of LiMn0.25Fe0.75PO4 As a Cathode Material for Lithium Ion Batteries

Fluorination Effect on Lithium- and Manganese-Rich Layered Oxide Cathodes

Synthesis of MnO-LiF composite cathode material using NH4F as a fluorine source

Synthesis Mechanism and Characterization of LiMn 0.5 Fe 0.5 PO 4 /C Composite Cathode Material for Lithium -Ion Batteries