Abstract:Li-Ion batteries (LIBs) are approaching their energy limits imposed by their intercalation chemistry nature. As alternatives, multivalent (MV) chemistries bring both promises and challenges, with the main obstacle being the sluggish diffusion of MV-cations due to their strong electrostatic interaction with host lattices. In this work, we demonstrated that polyanion based robust crystal architecture could enable ultrafast and reversible Zn2+-intercalation and de-intercalation at a high working voltage. The nominal bivalence of Zn2+ was successfully delocalized by multiple atoms through the p-d hybridization between the V-d and O-p orbitals; hence the inserted Zn2+ only bears an effective charge of 1.336, rendering its high mobility. The novel aqueous rechargeable 1.7 V Zn/LiV2(PO4)(3) cell based on such a mechanism delivers a high power density (8000 W kg(-1) at 60C) comparable to supercapacitors, and a high energy density (218 W h kg(-1) at 1C) close to LIBs, with an extraordinarily long cycle life of 4000 cycles. All of these parameters far exceed those of Zn batteries reported so far. The cell-level volumetric and specific energy densities of the Zn/LiV2(PO4)(3) cell are 320 W h L-1 and 150 W h kg(-1), respectively, which are even better than those of first-generation LIBs. Combined with the intrinsic safety of its aqueous chemistry and its wide working temperature range, this cell makes a strong candidate for automotive applications.

An Aqueous Rechargeable Lithium Battery with Good Cycling Performance

Superlattice Formation of Crystal Water in Layered Double Hydroxides for Long‐Term and Fast Operation of Aqueous Rechargeable Batteries

An Aqueous Rechargeable Lithium Battery Using Coated Li Metal as Anode

Aqueous Rechargeable Zinc/Aluminum Ion Battery with Good Cycling Performance

Aqueous Rechargeable Batteries For Large-Scale Energy Storage

An Aqueous Rechargeable Lithium Battery Based on Doping and Intercalation Mechanisms

ChemInform Abstract: Aqueous Rechargeable Batteries for Large‐Scale Energy Storage

Aqueous rechargeable lithium battery (ARLB) based on LiV3O8 and LiMn2O4 with good cycling performance

A Fully Aqueous Hybrid Electrolyte Rechargeable Battery with High Voltage and High Energy Density

Aqueous electrolyte with moderate concentration enables high-energy aqueous rechargeable lithium ion battery for large scale energy storage

Aqueous Rechargeable Li+/Na+Hybrid Ion Battery with High Energy Density and Long Cycle Life

Environmentally-Friendly Aqueous Li (or Na)-Ion Battery with Fast Electrode Kinetics and Super-Long Life

Aqueous rechargeable lithium batteries as an energy storage system of superfast charging

An Aqueous Rechargeable Lithium Battery of Excellent Rate Capability Based on A Nanocomposite of Moo3 Coated with Ppy and Limn2o4

Research Progress of the Aqueous Electrolyte Rechargeable Lithium Ion Battery

Long-Lived Aqueous Rechargeable Lithium Batteries Using Mesoporous Liti2(Po4)(3)@C Anode

A Rechargeable Aqueous Zn2+-battery with High Power Density and a Long Cycle-Life

An Aqueous Rechargeable Copper Ammonium Hybrid Battery with Good Cycling Performance

Aqueous Rechargeable Lithium Batteries Using Nav6o15 Nanoflakes As High Performance Anodes

A Class of Liquid Anode for Rechargeable Batteries with Ultralong Cycle Life.

Aqueous Dual-Ion Battery Based on Hematite Anode with Exposed {104} Facets.