High Permittivity and Low Loss Dielectric Ceramics Ba5LnNiNb9O30 (ln: La, Nd and Sm).

Liang Fang,Sensen Meng,Changzheng Hu

DOI: https://doi.org/10.1002/chin.200719009

2007-01-01

ChemInform

Abstract:ChemInform is a weekly Abstracting Service, delivering concise information at a glance that was extracted from about 200 leading journals. To access a ChemInform Abstract, please click on HTML or PDF.

What problem does this paper attempt to address?

High permittivity and low loss dielectric ceramics Ba5LnNiNb9O30 (Ln = La, Nd and Sm)

Liang Fang,Sen S. Meng,Chang-Zheng Hu

DOI: https://doi.org/10.1016/j.jallcom.2006.04.002

IF: 6.2

2007-01-01

Journal of Alloys and Compounds

Abstract:Three novel Ba5LnNiNb9O30 (Ln=La, Nd and Sm) ceramics were prepared and characterized in the BaO–Ln2O3–NiO–Nb2O5 system. All three compounds are paraelectric phases adopting the filled tetragonal tungsten bronze (TB) structure at room temperature. At 1MHz, Ba5LnNiNb9O30 ceramics have a high dielectric constants in the range 193–245.3, a low dielectric loss in range 0.0059–0.0087, and the temperature coefficients of the dielectric constant (τɛ) in the range −1140 to −1310ppm°C−1.
High Dielectric Constant and Low-Loss Dielectric Ceramics of Ba(5)Lnznnb(9)O(30) (ln = La, Nd and Sm)

Liang Fang,Qian Yu,Chang-zheng Hu,Hui Zhang

DOI: https://doi.org/10.1016/j.matlet.2007.01.068

IF: 3

2007-01-01

Materials Letters

Abstract:Polycrystalline Ba(5)LnZnNb(9)O(30) (Ln=La, Nd and Sm) ceramics were prepared as single-phase materials through conventional solid-state ceramics route. The structure was characterized by X-ray diffraction methods and scanning electron microscopy (SEM) and the dielectric properties were measured from - 120 degrees C to 150 degrees C. All three compounds are paraelectric phases adopting the filled tetragonal tungsten-bronze (TB) structure at room temperature, and the Curie temperature (at 1 MHz) were -60, -25 and -5 degrees C for Ba5LaZnNb9O30, Ba5NdZnNb9O30, and Ba5SmZnNb9O30 respectively. At 1 MHz their dielectric constant (epsilon(r)) varies from 258 to 310, dielectric loss (tan delta) from 0.0033 to 0.0068, and the temperature coefficients of the dielectric constant (tau(epsilon)) from - 1220 to - 1390 ppm degrees C-1. (c) 2007 Elsevier B.V. All rights reserved.
Characterization and Properties of New Dielectric Ceramics Ba5LnZnNb9O30(Ln=La, Nd and Sm)

Zhu Wen-feng,Hu Chang-zheng,Wu Bo-Lin,Fang Liang

DOI: https://doi.org/10.1016/s1003-6326(06)60251-3

2006-01-01

Abstract:Three novel dielectric ceramics Ba5LnZnNb9O30 (Ln= La, Nd and Sm) were synthesized and characterized in the BaO-Ln2O3-ZnO-Nb2O5 quaternary system, which formed the filled tungsten-bronze structures. The present ceramics exhibit high dielectric constant (ɛr) up to 310, low dielectric loss in the level of 10−3 at 1 MHz. Meanwhile, the temperature coefficients of the dielectric constant (τɛ) of Ba5LnZnNb9O30 varies from −1 390×10−6 to −1 220×10−6/°C as the radius of Ln3+ increases. The present ceramics are promising candidates for high dielectric constant and low loss dielectric ceramics.
Characterization and Dielectric Properties of Ba5LnNiTa9O30 (ln = La, Nd and Sm) Ceramics

L. Fang,H. Zhang,T. H. Huang,F. C. Meng,J. F. Yang

DOI: https://doi.org/10.1007/s10832-006-4299-7

2006-01-01

Journal of Electroceramics

Abstract:Three novel Ba 5 LnNiTa 9 O 30 (Ln = La, Nd and Sm) ceramics were prepared and characterized in the BaO-Ln 2 O 3 -NiO-Ta 2 O 5 system. All three compounds adopted the filled tetragonal tungsten bronze (TB) structure at room temperature. The present ceramics exhibited relaxor behavior, and the Curie temperature (at 10kHz) were −130, −80 and −45°C for Ba 5 LaNiTa 9 O 30 , Ba 5 NdNiTa 9 O 30 , and Ba 5 SmNiTa 9 O 30 respectively. At room temperature, Ba 5 LnNiTa 9 O 30 ceramics have a high dielectric constants in the range 102∼118, a low dielectric loss in range 0.0019∼0.0036, and the temperature coefficients of the dielectric constant (τ ɛ ) in the range −320∼−460 ppm°C −1 (at 1 MHz).
Structural and Dielectric Properties of Ba5LnSn3Nb7O30 (ln=la, Nd) Ceramics

L Fang,L Chen,H Zhang,CL Diao,RZ Yuan

DOI: https://doi.org/10.1016/j.matlet.2004.03.042

IF: 3

2004-01-01

Materials Letters

Abstract:Two novel Ba5LnSn3Nb7O30 (Ln=La, Nd) ceramics were prepared and characterized. Both compounds are paraelectric phases adopting the filled tetragonal tungsten bronze (TB) structure at room temperature. Ba5LaSn3Nb7O30 and Ba5NdSn3Nb7O30 ceramics show high dielectric constant of 171 and 182 together with low dielectric loss 1.2×10-3 and 1.8×10-3 at 1 MHz, respectively. In comparison with dielectric ceramics with TB structure in BaO–Ln2O3–TiO2–Ta2O5 (Ln=La, Nd) system, the temperature coefficients of the dielectric constant (τε) are significantly reduced.
Low‐firing and Temperature Stable Microwave Dielectric Ceramics: Ba2LnV3O11 (ln = Nd, Sm)

Chunchun Li,Huaicheng Xiang,Minyu Xu,Jibran Khaliq,Junqi Chen,Liang Fang

DOI: https://doi.org/10.1111/jace.15251

IF: 4.186

2017-01-01

Journal of the American Ceramic Society

Abstract:Low-firing and temperature stable microwave dielectric ceramics of Ba(2)LnV(3)O(11) (Ln=Nd, Sm) were prepared by solid-state reaction. X-ray diffraction (XRD) and scanning electron microscopy (SEM) were used to investigate the phase purity, crystal structure, sintering behavior, and microstructure. The XRD patterns indicated that Ba(2)LnV(3)O(11) (Ln=Nd, Sm) ceramics belong to monoclinic crystal system with P2(1)/c space group in the whole sintering temperature range (800 degrees C -900 degrees C). Both ceramics could be well densified at 880 degrees C for 4hours with relative densities higher than 96%. The Ba(2)LnV(3)O(11) (Ln=Nd, Sm) samples sintered at 880 degrees C for 4hours exhibited excellent microwave dielectric properties: epsilon(r)=12.05, Qxf=23010GHz, (f)=-7.7ppm/degrees C, and epsilon(r)=12.19, Qxf=27120GHz, (f)=-16.2ppm/degrees C, respectively. Besides, Ba(2)LnV(3)O(11) (Ln=Nd, Sm) ceramics could be well co-fired with the silver electrode at 880 degrees C.
High Permittivity and Low Loss Dielectric Ceramics in the BaO–La2O3–TiO2–Ta2O5 System

XM Chen,YH Sun,XH Zheng

DOI: https://doi.org/10.1016/s0955-2219(02)00372-2

IF: 5.7

2003-01-01

Journal of the European Ceramic Society

Abstract:Dielectric ceramics were synthesized and characterized in the BaO-La2O3-TiO2-Ta2O5 quaternary system for the three typical compositions: Ba3La3Ti5Ta5O3O, Ba4La2Ti4Ta6O30 and Ba5LaTi3Ta7O30, which formed the filled tungsten-bronze structures. The present ceramics indicated high dielectric constant 6 (127.7-148.1) and low dielectric loss tandelta (in the order of 10(-4)-10(-3) at 1 MHz). Meanwhile, the temperature coefficient of dielectric constant tau(epsilon) varied from -728 to -1347 ppm/degreesC with increasing Ba and Ta and decreasing La and Ti concentration in the temperature range of 20-85 degreesC. The present ceramics are promising candidates for high-epsilon and low loss dielectric ceramics, and the suppression of tau(epsilon) should be the primary issue in the future work. (C) 2003 Elsevier Science Ltd. All rights reserved.
Preparation and Characterization of New Dielectric Ceramics Ba5LnTi2Nb3O18 (ln = La, Nd)

Liang Fang,Hui Zhang,L. Chen,R. Z. Yuan,R. Dronskowski

DOI: https://doi.org/10.1007/s10854-005-4957-6

2005-01-01

Journal of Materials Science Materials in Electronics

Abstract:Two new A6B5O18 type cation-deficient perovskites Ba5LnTi2Nb3O18 (Ln = La, Nd) were prepared by the conventional solid-state reaction route. The phase and structure of the ceramics were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM). Both compounds crystallize in the trigonal system. Ba5LaTi2Nb3O18 has a dielectric constant of 56.6, a high quality factors (Q u × f > 16,700 at 4.3331 GHz), and a relatively large temperature coefficient of resonant frequency (τ f ) + 142 ppm°C−1 at room temperature; Ba5NdTi2Nb3O18 has a higher dielectric constant of 47.3 with high quality factors Q u × f > 15,000 at 4.6830 GHz, and τ f + 128 ppm°C−1.
High Dielectric Strength and Energy Storage Density in Ba6−3xLn8+2xTi18O54 (ln = La, Sm) Low-Loss Dielectric Ceramics

L. Zhong,X. L. Zhu,S. Y. Wu,X. M. Chen

DOI: https://doi.org/10.1007/s10854-013-1308-x

2013-01-01

Journal of Materials Science Materials in Electronics

Abstract:Dielectric strength and energy storage density in Ba6−3x Ln8+2x Ti18O54 (Ln = La, Sm) low-loss dielectric ceramics have been investigated together with their composition and microstructure dependences. The dielectric strength increases with increasing x at first, reaches the maximum around x = 2/3 and turns to decrease for x = 3/4, except the composition x = 3/4 for Ba6−3x Sm8+2x Ti18O54, while the energy storage density decreases generally with increasing x. The maximum energy storage density is 0.38 J/cm3 under an electric field of 26 MV/m for x = 1/4 in Ba6−3x La8+2x Ti18O54. The highest dielectric strength and energy storage density are obtained in the present ceramics with the maximum bulk density and the minimum grain size. Compared with the ferroelectric materials, very low dielectric loss combined with the excellent temperature stability provide the essential advantages for the energy storage applications.
Preparation, characterization and dielectric properties of Ba5LnZnTa9O30 (Ln=La, Sm) ceramics

L Fang,H Zhang,J.F Yang,R.Z Yuan,H.X Liu

DOI: https://doi.org/10.1016/j.materresbull.2003.12.004

IF: 5.6

2004-01-01

Materials Research Bulletin

Abstract:Ba5LnZnTa9O30 (Ln=La, Sm) ceramics were prepared by high temperature solid-state reaction route. The samples were characterized by X-ray diffraction, scanning electron microscopy (SEM), and differential scanning calorimetry (DSC) methods. They belong to paraelectric phase of filled tetragonal TB structure at room temperature with unit cell a=12.5909(4)Å, c=3.9622(2)Å for Ba5LaZnTa9O30; and a=12.5777(4)Å, c=3.9544(2)Å for Ba5SmZnTa9O30. At 1MHz, Ba5LaZnTa9O30 has high dielectric constants of 89 with low dielectric loss 0.0067, and temperature coefficients of the dielectric constant (τε) −811ppm°C−1; Ba5LaZnTa9O30 has dielectric constants of 74 with low dielectric loss 0.0035, and τε −474ppm°C−1.
New Microwave Dielectric Ceramics Baln(2)(Moo4)(4) (Ln = Nd And Sm) With Low Loss

Di Zhou,Li-Xia Pang,Jing Guo,Ying Wu,Gao-Qun Zhang,Wei Dai,Hong Wang,Xi Yao

DOI: https://doi.org/10.1111/j.1551-2916.2011.04727.x

IF: 4.186

2011-01-01

Journal of the American Ceramic Society

Abstract:In the present work, a pure monoclinic phase of BaNd2(MoO4)(4) and BaSm2(MoO4)(4) was formed at 850 degrees C and 600 degrees C, respectively, via a solid-state reaction method. The ceramic samples were found to be well densified at 960 degrees C. Dense and homogeneous microstructures were revealed from the scanning electron microscopy. The microwave dielectric behaviors were studied as a function of sintering temperature and characterized in the temperature range 25 degrees C-120 degrees C. The best properties were obtained in ceramics sintered at 960 degrees C with a permittivity similar to 11.7, a Q x f value of 45 000 GHz and a temperature coefficient of frequency about -41 ppm/degrees C for BaNd2(MoO4)(4) ceramic at 9.9 GHz, and a permittivity similar to 11.8, a Q x f value of 20 000 GHz, and a temperature coefficient of frequency about -34 ppm/degrees C for BaSm2(MoO4)(4) ceramic at 9.7 GHz, respectively.
Ln(2)Mo(3)O(12) (Ln = La, Nd): A Novel Group Of Low Loss Microwave Dielectric Ceramics With Low Sintering Temperature

Li-Xia Pang,Guo-Bin Sun,Di Zhou

DOI: https://doi.org/10.1016/j.matlet.2010.09.064

IF: 3

2011-01-01

Materials Letters

Abstract:Ln(2)Mo(3)O(12) (Ln = La, Nd) ceramics with a defect scheelite related structure were prepared via a solid state reaction method. The Ln(2)Mo(3)O(12) ceramics sintered at 930 degrees C for 2 h exhibited a low dielectric permittivity of 10.1, a high quality factor (Qf value) of 60,000 GHz and a temperature coefficient of -80 ppm/degrees C at 12.7 GHz. The Nd2Mo3O12 ceramics sintered at 945 degrees C for 2 h possessed a dielectric permittivity of 8.2, a Qf value of 80,000 GHz, and a temperature coefficient of -60 ppm/degrees C at 15.8 GHz. This group of ceramics could be good candidates for microwave substrate applications. (C) 2010 Elsevier B.V. All rights reserved.
High Permittivity Li And Al Doped Nio Ceramics

Yh Lin,Jf Wang,L Jiang,Y Chen,Cw Nan

DOI: https://doi.org/10.1063/1.1827937

IF: 4

2004-01-01

Applied Physics Letters

Abstract:High-permittivity dielectric NiO-based ceramics co-doped with Li and Al (LANO) have been prepared by a traditional solid-state synthesis. Analyses of the ceramic microstructure and composition indicate that Al ions are distributed in grain boundaries, and that uniform boundaries indexed as NiAl2O4 surround the grains. The concentration of Al has a remarkable effect on the dielectric properties of the LANO ceramics. The dielectric constant remains almost constant (similar to10(4)-10(5)) at low frequency and has a steplike decrease toward higher frequencies. The high-dielectric-constant response of the LANO ceramics is mainly enhanced by Maxwell-Wagner polarization. (C) 2004 American Institute of Physics.
High Dielectric Permittivity and Ultralow Dielectric Loss in Nb-doped SrTiO3 Ceramics

Lichen Luo,Jinglei Li,Mingwen Wang,Shuai Yang,Jie Wu,Xiangyu Gao,Chunchun Li,Wenya Du,Lin Zhang,Fei Li

DOI: https://doi.org/10.1016/j.ceramint.2022.06.157

IF: 5.532

2022-01-01

Ceramics International

Abstract:In this study, we prepared a series of Nb-doped SrTiO3 ceramics sintered in both air and N-2 atmospheres. The X-ray diffraction (XRD) analysis indicated that all samples had a pure cubic phase perovskite structure with no secondary phase. The dielectric test showed that the Nb-doped SrTiO3 ceramics had a high dielectric permittivity (> 3 x 10(4)) and low dielectric loss (< 0.004) over a broad temperature range from-100 to 300 ?C with a breakdown strength over 20 kV/cm. The dielectric performance is attributed to the designated Ti '(Ti)- V-O(..)- Ti-Ti ' deep-lattice-defect states localising weak-hopping electrons to generate high defect-dipole concentrations, as verified by systematic X-ray photoelectron spectroscopy (XPS) experiments. This study offers a route for designing other types of high dielectric permittivity ceramics.
High Εr and Low Loss Microwave Dielectric Ceramics Ba3LiNb3−xTaxTi5O21

Liang Fang,Meixia Wu,Qinwen Liu,Ying Tang,Huanfu Zhou,Hui Zhang

DOI: https://doi.org/10.1016/j.matchemphys.2012.07.032

IF: 4.778

2012-01-01

Materials Chemistry and Physics

Abstract:High dielectric constant and low loss microwave dielectric ceramics in the system Ba3LiNb3-xTaxTi5O21 (0 <= x <= 3) have been prepared through solid state ceramic route. The structure and microstructure of the compositions have been studied using powder X-ray diffraction and Scanning electron microscopic studies. The ceramics could be well densified under 1140 degrees C and exhibited a single hexagonal phase through the entire range of compositions. They show a linear variation of dielectric properties with the value of x. Their dielectric constant (E,) varies from 78 to 55.5, quality factor Q x f increases from 9780 to 18,480 GHz and temperature variation of resonant frequency reduces from 205 to +70 ppm degrees C (1) as the content of Ta increases. (C) 2012 Elsevier B.V. All rights reserved.
Synthesis, Characterization, and Dielectric Properties of Low Loss LaBO3 Ceramics

Xingyu Chen,Shuxin Bai,Ming Li,Weijun Zhang

DOI: https://doi.org/10.1016/j.jeurceramsoc.2013.07.005

IF: 5.7

2013-01-01

Journal of the European Ceramic Society

Abstract:The preparation, sintering behaviour, and dielectric properties of low loss LaBO3 ceramics have been investigated. Single-phase LaBO3 powder was synthesized by the conventional solid-state ceramics route and dense ceramics (relative density >96%) with uniform microstructure (grain size ∼30μm) were obtained by sintering at 1300°C in air. The electrical conductivity of LaBO3 follows the Arrhenius law and the related activation energies for electrical conduction of bulk and grain boundary are 0.62eV and 0.90eV, respectively. The LaBO3 ceramics sintered at 1300°C exhibit excellent microwave dielectric properties with a relative permittivity, ɛr∼11.8, a quality factor, Q×f0 value ∼76,869GHz (at ∼15GHz), and a negative temperature coefficient of resonant frequency τf∼−52ppm/°C.
Temperature-stable and Low Loss Fe-containing Dielectrics in BaO-Ln2O3-Fe2O3-Ta2O5 System

Liang Fang,Zhao Yang,Hui Zhang,Chunchun Li,Xiyang Peng,Changzheng Hu,Dongjin Chu

DOI: https://doi.org/10.1007/s10854-010-0286-5

2011-01-01

Journal of Materials Science Materials in Electronics

Abstract:Polycrystalline samples of Ba4Ln2Fe2Ta8O30 (Ln = La and Nd) were prepared by a high temperature solid-state reaction technique. The formation, structure, dielectric and ferroelectric properties of the compounds were studied. Both compounds are found to be paraelectrics with filled tetragonal tungsten bronze (TB) structure at room temperature. Dielectric measurements revealed that the present ceramics have exceptional temperature stability, a relatively small temperature coefficient of dielectric constant (τ ε ) of −25 and −58 ppm/°C, with a high dielectric constant of 118 and 96 together with a low dielectric loss of 1.2 × 10−3 and 2.8 × 10−3 (at 1 MHz) for Ba4La2Fe2Ta8O30 and Ba4Nd2Fe2Ta8O30, respectively. The measured dielectric properties indicate that both materials are possible candidates for the fabrication of discrete multilayer capacitors in microelectronic technology.
Dielectric properties of low-temperature sintered Ba(Fe0.5Nb0.5)O3 with BaCu(B2O5) addition

Ying Lin,Zhenfeng Zhu,Haibo Yang

DOI: https://doi.org/10.3139/146.110599

2011-01-01

International Journal of Materials Research

Abstract:Abstract Low loss and low-temperature sintered Ba(Fe0.5Nb0.5)O3 (BFN) ceramics were prepared via a conventional solidstate method with BaCu(B2O5) (BCB) addition. The effect of the BCB content on the dielectric properties of the BFN ceramics was investigated. Low amounts of BCB can significantly reduce the dielectric loss of BFN ceramic from 2 to 0.2, as well as the sintering temperature from 1400°C to 1100°C. The results show that the as-sintered BFN ceramic is a promising candidate material for use in capacitors.
Ba4Ln2Fe2Nb8O30(Ln = Eu, Gd) Ferroelectric Ceramics

Changzheng Hu,Xiyang Peng,Chunchun Li,Liang Fang,Laijun Liu

DOI: https://doi.org/10.1080/00150193.2010.481999

2010-01-01

Ferroelectrics

Abstract:Ba(4)Ln(2)Fe(2)Nb(8)O(30) (Ln = Eu and Gd) ceramics were synthesized by high temperature solid state reaction. The phase composition, microstructure, dielectric and ferroelectric properties of them were characterized. Both ceramics adopt filled tetragonal tungsten bronze structure at room temperature. The diffusive phase transitions were observed for Ba4Eu2Fe2Nb8O30 and Ba4Gd2Fe2Nb8O30 around 163 degrees C and 150 degrees C, respectively. Ba4Eu2Fe2Nb8O30 and Ba4Gd2Fe2Nb8O30 ceramics are classical ferroelectrics at room temperature and show high dielectric constant of 118 and 160 and low dielectric loss 0.022 and 0.054 at 1 MHz, respectively. The remnant polarizations (2P(r)) are 3.9 mu C/cm(2) for Ba4Eu2Fe2Nb8O30 and 1.71 mu C/cm(2) for Ba4Gd2Fe2Nb8O30.
Ba(4)Ln(2)Fe(2)Nb(8)O(30) (ln = Eu, Gd) Ferroelectric Ceramics

Changzheng Hu,Xiyang Peng,Chunchun Li,Liang Fang,Laijun Liu

DOI: https://doi.org/10.1080/00150193.2010.481999

2010-01-01

Ferroelectrics

Abstract:Ba4Ln2Fe2Nb8O30 (Ln = Eu and Gd) ceramics were synthesized by high temperature solid state reaction. The phase composition, microstructure, dielectric and ferroelectric properties of them were characterized. Both ceramics adopt filled tetragonal tungsten bronze structure at room temperature. The diffusive phase transitions were observed for Ba4Eu2Fe2Nb8O30 and Ba4Gd2Fe2Nb8O30 around 163°C and 150°C, respectively. Ba4Eu2Fe2Nb8O30 and Ba4Gd2Fe2Nb8O30 ceramics are classical ferroelectrics at room temperature and show high dielectric constant of 118 and 160 and low dielectric loss 0.022 and 0.054 at 1 MHz, respectively. The remnant polarizations (2Pr) are 3.9μC/cm2 for Ba4Eu2Fe2Nb8O30 and 1.71μC/cm2 for Ba4Gd2Fe2Nb8O30.

High Permittivity and Low Loss Dielectric Ceramics Ba5LnNiNb9O30 (ln: La, Nd and Sm).

High permittivity and low loss dielectric ceramics Ba5LnNiNb9O30 (Ln = La, Nd and Sm)

High Dielectric Constant and Low-Loss Dielectric Ceramics of Ba(5)Lnznnb(9)O(30) (ln = La, Nd and Sm)

Characterization and Properties of New Dielectric Ceramics Ba5LnZnNb9O30(Ln=La, Nd and Sm)

Characterization and Dielectric Properties of Ba5LnNiTa9O30 (ln = La, Nd and Sm) Ceramics

Structural and Dielectric Properties of Ba5LnSn3Nb7O30 (ln=la, Nd) Ceramics

Low‐firing and Temperature Stable Microwave Dielectric Ceramics: Ba2LnV3O11 (ln = Nd, Sm)

High Permittivity and Low Loss Dielectric Ceramics in the BaO–La2O3–TiO2–Ta2O5 System

Preparation and Characterization of New Dielectric Ceramics Ba5LnTi2Nb3O18 (ln = La, Nd)

High Dielectric Strength and Energy Storage Density in Ba6−3xLn8+2xTi18O54 (ln = La, Sm) Low-Loss Dielectric Ceramics

Preparation, characterization and dielectric properties of Ba5LnZnTa9O30 (Ln=La, Sm) ceramics

New Microwave Dielectric Ceramics Baln(2)(Moo4)(4) (Ln = Nd And Sm) With Low Loss

Ln(2)Mo(3)O(12) (Ln = La, Nd): A Novel Group Of Low Loss Microwave Dielectric Ceramics With Low Sintering Temperature

High Permittivity Li And Al Doped Nio Ceramics

High Dielectric Permittivity and Ultralow Dielectric Loss in Nb-doped SrTiO3 Ceramics

High Εr and Low Loss Microwave Dielectric Ceramics Ba3LiNb3−xTaxTi5O21

Synthesis, Characterization, and Dielectric Properties of Low Loss LaBO3 Ceramics

Temperature-stable and Low Loss Fe-containing Dielectrics in BaO-Ln2O3-Fe2O3-Ta2O5 System

Dielectric properties of low-temperature sintered Ba(Fe<sub>0.5</sub>Nb<sub>0.5</sub>)O<sub>3</sub> with BaCu(B<sub>2</sub>O<sub>5</sub>) addition

Ba<sub>4</sub>Ln<sub>2</sub>Fe<sub>2</sub>Nb<sub>8</sub>O<sub>30</sub>(Ln = Eu, Gd) Ferroelectric Ceramics

Ba(4)Ln(2)Fe(2)Nb(8)O(30) (ln = Eu, Gd) Ferroelectric Ceramics