Ba<sub>4</sub>Ln<sub>2</sub>Fe<sub>2</sub>Nb<sub>8</sub>O<sub>30</sub>(Ln = Eu, Gd) Ferroelectric Ceramics

Changzheng Hu,Xiyang Peng,Chunchun Li,Liang Fang,Laijun Liu
DOI: https://doi.org/10.1080/00150193.2010.481999
2010-01-01
Ferroelectrics
Abstract:Ba(4)Ln(2)Fe(2)Nb(8)O(30) (Ln = Eu and Gd) ceramics were synthesized by high temperature solid state reaction. The phase composition, microstructure, dielectric and ferroelectric properties of them were characterized. Both ceramics adopt filled tetragonal tungsten bronze structure at room temperature. The diffusive phase transitions were observed for Ba4Eu2Fe2Nb8O30 and Ba4Gd2Fe2Nb8O30 around 163 degrees C and 150 degrees C, respectively. Ba4Eu2Fe2Nb8O30 and Ba4Gd2Fe2Nb8O30 ceramics are classical ferroelectrics at room temperature and show high dielectric constant of 118 and 160 and low dielectric loss 0.022 and 0.054 at 1 MHz, respectively. The remnant polarizations (2P(r)) are 3.9 mu C/cm(2) for Ba4Eu2Fe2Nb8O30 and 1.71 mu C/cm(2) for Ba4Gd2Fe2Nb8O30.