Expandable Graphite-Filled Polymer (LDPE) Composite Film Materials for Flame Retardancy

Qingze Jiao

2007-01-01

Applied Mechanics and Materials

Abstract:The paper introduces a newly renovated flame-retarding material by adding to the retardant the intumescent flame retardant made from ammonium polyphosphate(APP)and pentaerythritol(PER)plus expandable graphite(EG)powder into LDPE.As we know,resin LDPE has always been used to produce plastic films for its lower viscosity and higher melting strength in making films.However,its oxygen index of LDPE is just 17.2%,in addition to its unfavorable feature likely to get ignited,which naturally restrained its applications for packaging.To solve the problem,it is recommended to use environment-friendly intumescent flame retardants,ammonium polyphosphate(APP)/pentaerythritol(PER)and expandable graphite(EG)powder filled in with plastic cables.For the above purposes,the present paper is mainly to introduce the combustion mechanism of low density polyethylene,APP/PER/EG,the influence of adding of APP/PER and EG on the mechanical properties of the composite,with the stress of the preparation process of the flame retardant films and ways for optimizing the formulation of the system of APP/PER/EG/LDPE.When the flame retardant LDPE films are made,each section temperature of the twin screw extruder should be 165 ℃,170 ℃,170 ℃,170 ℃,175 ℃,175 ℃.The results of our research show that to some extent,APP/PER/EG may have synergistic effect on the flame retardants of LDPE films.Our research also proves that there exists great potentiality to improve the flame retardancy and anti-dripping melting risks by filling such materials as APP/PER/EG.In addition,our tests prove that on the condition when the mass ratio of APP,PER,and EG to LDPE is 16∶8∶6∶100 and the total flame retardant mass content was 30%,there appears the possibility that the LOI was 27.5% and the tensile strength would reach their highest value,14.75 MPa.