Abstract:Polyacrylate (PAE)/nano-silica (SiO2) hybrids were prepared by an in situ sol–gel process of tetraethyl orthosilicate in the presence of PAE toluene solution. The hybrid coatings were fabricated using a PAE/SiO2 suspension by the traditional casting. Their intermolecular interaction and morphology, as well as thermal, mechanical, and optical properties, were investigated using Fourier transform infrared spectroscopy, field-emission scanning electron microscope, differential scanning calorimetry and TG/DTA thermogravimetric analysis, coating impact testing, and UV–Vis spectroscopy, respectively. At the same time, their abrasive properties were carried out by abrasion resistance and nanoindentation tests. The results indicate that silica nanoparticles, with diameter about 30 nm, can disperse homogeneously in the PAE matrix, where hydrogen bonds between the PAE and nano-silica are formed. Therefore, homogeneous dispersion of nano-silica particles provides high transparency for the PAE/SiO2 hybrid coating as the size of nano-silica phase is much smaller than the wavelength (390–770 nm) of visible light. PAE/nano-silica hybrid coatings have increased T g and thermal stability including the onset decomposition temperature, 10 % weight loss temperature, and char at 700 °C. Additionally, the incorporation of nano-silica particles improves the glossiness of the PAE/nano-silica hybrid coatings and enhances their abrasion resistance and surface hardness. The nano-silica content has obvious effect on the thermal, mechanical, optical, and anti-abrasion properties of PAE/SiO2 hybrid coatings. With the consideration of all the properties of hybrid coatings, the PAE/SiO2 hybrid containing 10 phr of nano-silica has the optimal composition. These PAE/nano-silica hybrid coatings have potential applications in high-performance hologram image recording.

Co-solvents Induced Sol-Gel-derived SiO_2/polyacrylate Composite Films

Co-solvents induced sol-gel-derived SiO2/polyacrylate composite films

Preparation of Organic/Inorganic Hybrid Polymer Emulsions with High Silicon Content and Sol-gel-derived Thin Films

The Mechanism of Silane Coupling Agents on the Properties of Polyacrylate/SiO_2 Hybrid Emulsions

Fabrication of chemically bonded polyacrylate/silica hybrid films with high silicon contents by the sol–gel method

Preparation and Dielectric Properties of Polyimide/silica Nanocomposite Films Prepared from Sol–gel and Blending Process

Surface Modification of Functionalized Polyacrylate Emulsion and Properties of the Product

Film-Formation of Polyacrylate/Silica Composite Latexes by Sol-Gel Process

Synthesis and Characterization of Nano-silica/Polyacrylate Composite Emulsions by Sol-gel Method and In-Situ Emulsion Polymerization

Preparation and Properties of High Silicon Content Waterborne Wood Coatings

Preparation of acrylate polymer/silica nanocomposite particles with high silica encapsulation efficiency via miniemulsion polymerization

Preparation of polyacrylate/nano-SiO2composite emulsion by Pickering emulsion polymerization and its potential application in coating materials

Hydroxyl Derived the Preparation and Film Formation of Poly(Styrene-co-Acrylate)/Silica Hybrid Emulsion

Synthesis of Nano-silica/Fluorinated Polyacrylate Composite Emulsions Via Miniemulsion Polymerization and Study on Its Properties

Facile fabrication of superhydrophilic poly(styrene-co-acrylate)/SiO2 composite materials by conventional emulsion polymerization

Properties of silica/polymer composite emulsions prepared with different silica sources

Thermal Stability and Abrasion Resistance of Polyacrylate/nano-Silica Hybrid Coatings

Synthesis, Characterization and Thermal Properties of Some Organic-inorganic Hybrid Composites

Fabrication of Hydrophobic Composite Films by Sol-Gel Process Between POSS -Containing Fluorinated Polyacrylate Latexes and Colloidal Silica Particles

Study on fluoro-acrylate polymer/SiO2 hybrids prepared by sol-gel process

Synthesis and Characterization of Poly(fluorinated Styrene-Acrylate)/silica Nanocomposites