Covalent Organic Framework-Supported Metallocene for Ethylene Polymerization
Bangban Zhu,Kan Liu,Liqiong Luo,Ziyang Zhang,Yangke Xiao,Minghao Sun,Suyun Jie,Wen-Jun Wang,Jijiang Hu,Shengbin Shi,Qingyue Wang,Bo-Geng Li,Pingwei Liu
DOI: https://doi.org/10.1002/chem.202300913
2023-09-26
Chemistry
Abstract:The loading of homogeneous catalysts with support can dramatically improve their performance in olefin polymerization. However, the challenge lies in the development of supported catalysts with well-defined pore structures and good compatibility to achieve high catalytic activity and product performance. Herein, we report the use of an emergent class of porous material-covalent organic framework material (COF) as a carrier to support metallocene catalyst-Cp2 ZrCl2 for ethylene polymerization. The COF-supported catalyst demonstrates a higher catalytic activity of 31.1×106 g mol-1 h-1 at 140 °C, compared with 11.2×106 g mol-1 h-1 for the homogenous one. The resulting polyethylene (PE) products possess higher weight-average molecular weight (Mw ) and narrower molecular weight distribution (Ð) after COF supporting, that is, Mw increases from 160 to 308 kDa and Ð drops from 3.3 to 2.2. The melting point (Tm ) is also increased by up to 5.2 °C. Moreover, the PE product possesses a characteristic filamentous microstructure and demonstrates an increased tensile strength from 19.0 to 30.7 MPa and elongation at break from 350 to 1400 % after catalyst loading. We believe that the use of COF carriers will facilitate the future development of supported catalysts for highly efficient olefin polymerization and high-performance polyolefins.