Abstract:Energy-efficient sol-gel synthesis was achieved through the microwave assisted self-combustion route to produce hexagonal Tungsten oxide semiconductor (WO3). The photocatalytic activity was enhanced by doping Cobalt (Co) into the crystalline structure of the nanoparticle, which were subsequently sintered at 400 °C for an hour. The structural and morphological properties of the Co-doped WO3 were revealed using X-ray diffraction (XRD) characterization. The nanoparticles exhibited an amorphous structure before annealing, due to the short heating time during combustion synthesis. Sintering the nanoparticle transformed the nanoparticle from a monoclinic phase to orthorhombic phase structure. Additional analysis techniques, including scanning electron microscopy (SEM), transmission electron microscopy (TEM) and energy dispersive X-ray spectrum analysis (EDS). To assess the photocatalytic performance of these particles, Acid Blue 74 (AB 74) was employed in photodegradation experiments under UV light irradiation within a semi-continuous reactor. The photodegradation of dye molecules was evaluated utilizing a UV-Vis spectrophotometer, and the mineralization efficiency of the dye was determined through total organic carbon analysis (TOC). The results indicated that the dimension of the synthesized nano catalyst fell within the range of 70-120 nm, and it exhibited the ability to completely degrade a solution with an initial dye concentration of 20 ppm within 60 min. Various parameters affecting the photocatalytic reaction, including the photocatalyst dosage, initial dye concentration, pH and temperature of the dye solution were also investigated. The experiments were designed using Response surface methodology (RSM), through which a mathematical model for the dye removal process was developed.

Synthesis of Co~IIW_(12)/SiO_2 and Photocatalytic Degradation of Orange II

Photodegradation of Orange Ii Using Waste Paper Sludge-Derived Heterogeneous Catalyst in the Presence of Oxalate under Ultraviolet Light Emitting Diode Irradiation

Visible-light Photocatalytic Decolorization of Orange II on Cu2O/ZnO Nanocomposites

Photocatalytic Degradation of Organic Dyes by H4SiW6Mo6O40/SiO2 Sensitized by H2O2

Efficient Degradation of Orange II by Core Shell CoFe2O4-CeO2 Nanocomposite with the Synergistic Effect from Sodium Persulfate.

Fe–Co-SBA Assisted by Visible Light Can Effectively Activate NaHSO3 or H2O2 for Enhanced Degradation of Orange Ⅱ: Activation of NaHSO3 Versus H2O2

Spinel-type Cobalt-Manganese Oxide Catalyst for Degradation of Orange II Using a Novel Heterogeneous Photo-Chemical Catalysis System

Persulfate Activation over CoFe2O4/CuS for Degradation of Orange II under Visible Light

In situ reduction for synthesis of nano-sized Cu2O particles on MgCuAl-LDH layers for degradation of orange II under visible light

Heterogeneous Activation of Persulfate by Bi2MoO6–CuS Composite for Efficient Degradation of Orange II under Visible Light

Magnetic core-shell CuFe2O4@C3N4 hybrids for visible light photocatalysis of Orange II

Activation of K<sub>2</sub>S<sub>2</sub>O<sub>8</sub> by Ni-Ce composite oxides for the degradation of orange II with visible light assistance

Improved degradation of Orange II by Fe<sub>3</sub>O<sub>4</sub>/NiO/NaHSO<sub>3</sub> system under visible light irradiation

Preparation of acidic Fe-SiO2 catalyst and its catalytic reactivity in photo-Fenton reaction

Bi2MoO6 Microspheres for the Degradation of Orange II by Heterogeneous Activation of Persulfate under Visible Light

Degradation of Orange II by Fe2O3 and CeO2 Nanocomposite when Assisted by NaHSO3

A novel heterogeneous Co(II)-Fenton-like catalyst for efficient photodegradation by visible light over extended pH

Bimetallic Fe/Ti‐Based Metal–Organic Framework for Persulfate‐Assisted Visible Light Photocatalytic Degradation of Orange II

TiO2-mediated Photocatalytic Degradation of Orange II with the Presence of Mn2+ in Solution

Photocatalytic degradation of acid blue 74 by Co: WO3 nanoparticles: Kinetics and response surface methodology studies

A Novel Fenton-like System of Fe2O3 and NaHSO3 for Orange II Degradation