Synthesis and Magnetic Propertise of CoFe_2O_4 Nanoparticles by Auto-Combustion Method
FENG Jin-Di,ZHANG Yue,LIU Yang,SHI Jing,XIONG Rui
2008-01-01
Abstract:CoFe_2O_4 nanopartieles were prepared by citric acid auto-combustion method,the as-burnt powders were calcined at different temperature,the morphology,component,and chemical bond were respectively studied by Scanning E- lectron Microscopy(SEM),x-ray Photoolectron Spectroscopy(XPS),and Infrared spectroscopy(IR),the crystal struc- ture of the as-burnt powders and products calcined at different temperature was characterized by X-Ray Diffraction(XRD), the results shows that the as-burnt powders were pure CoFe_2O_4 phase with high dispersibility and relatively low agglomera- tion,and the particle size is between 40 and 80nm,The magnetic hysteresis loops of the as-burnt powders and products cal- cined at different temperature were collected at room temperature(RT)using a vibrating sample magnetometer(VSM), the results shows that saturation magnetization(Ms),coercivity(He) and remanence ratio(Mr/Ms)were drastically de- pending upon the annealing temperature,Ms increased with increasing temperature,while Hc and Mr/Ms both reached maximum values as the as-burnt powders were calcined at 400℃,and Hc reached 3180Oe.