The Combination of Self-Produced Template Methodology and Self-Limitation Properties of Target Materials Towards Three-Dimensional Hierarchical Nanostructures

Chi Wu

2008-01-01

Abstract:A novel way to grow and assemble three-dimensional (3D) hierarchical nanostructures was described,where the combination of the self-produced template methodology and the self-limitation properties of the functional inorganic material's crystal were conducted in the reaction processes.The whole reaction process was simple,controllable and without the complicated post-treatment by the utilization of this strategy.Here,the rutile TiO2 3D hollow nanostructures could be achieved with a new simple chemical synthetic methodology.It was believed that the formation of rutile nanorods is actually the outward embodiment of the nature of the initial crystal structure,while the newly born O2 gas bubbles acted as the support for the construction of rutile TiO2 3D hollow nanostructures.Furthermore,VOOH hollow dandelions were synthesized owing to the planar sheet nature of the building blocks in the new-phased VOOH and the in-situ produced N2 gas bubbles as the templates that acted as the sheet-like nanounits' supporter.Also,titanate 3D tubular hierarchitectures were successfully prepared undergoing the self-produced template methodology coupled with precursor templating approach based on the similar strategy.The appearance of titanate nanoflakes is actually the outward embodiment of the internal crystal structure,while the sacrificed templating effect of the intermediate precursor of TiOxCl2-2x(EN)y is well understood.〖MQ(《2》B+18mm.40mm(8*3,36*2)-W%〗