Abstract:Cellulose is the most abundant nature polymer and the main component in all biomass. In this study, the degradation kinetic parameters and structure changes of microcrystalline cellulose (MCC), which served as fundamental studies for degradation of biomass in subcritical water, were investigated at the temperature range from 100 to 300 degrees C. The yield of the MCC residue began to decrease at 205 degrees C and reached the lowest value at 275 degrees C. However, it howed an increase at the temperature higher than 275 degrees C. The degradation area of MCC (205275 degrees C) was separated into zones 1 and 2 with 245 degrees C as a boundary. The activation energy (E), pre-exponential factor (A), and reaction order (n) of MCC in each zone were 226.5 kJ mol(-1), 2.3 x 10(23) s(-1), and 0.6 (zone 1) and 423.1 kJ mol(-1), 9.0 x 10(40) s(-1), and 0.5 (zone 2), respectively. There showed a breaking point of 245 degrees C for the Arrhenius plot in the reaction area. The surface morphology of the MCC residue had no significant change below 260 degrees C, as indicated by scanning electron microscopy (SEM) images. However, it was completely destroyed at the temperature above 275 degrees C, and MCC residues with strong pore structures were obtained at higher temperatures. The structures of the crystalline region of the MCC residue below 275 degrees C had no significant change, although 89.2% MCC was degraded at 275 degrees C. However, they nearly disappeared at higher temperatures with the steeply reducing crystallinity index of MCC at the same time. As for the degradation mechanism of MCC, it was proposed that only the surface of MCC was degraded at 205-245 degrees C and the hydrogen and glycosidic bonds on the interior of MCC fibrils were destroyed at the temperature range from 245 to 275 degrees C. Finally, the remaining MCC as well as generated oligomer and monomer were further degraded at higher temperatures.

Study on Saccharification of Microcrystalline Cellulose Hydrolysis in Supercritical Water

Supercritical Pretreatment and Hydrolyzation of Cellulose

The Ways of Factors Influencing High-Solid Enzymatic Hydrolysis of Sugarcane Bagasse Treated by Liquid Hot Water

Hydrolysis of lignocellulosic feedstock with supercritical water.

Evaluation of the Solvent Water Effect on High Solids Saccharification of Alkali-Pretreated Sugarcane Bagasse.

STUDY ON SACCHARIFICATION OF EUCALYPTUS LIGNOCELLULOSES HYDROLYSIS AND REACTION KINETICS IN SUPERCRITICAL WATER

Combined supercritical and subcritical process for cellulose hydrolysis to fermentable hexoses.

Supercritical hydrolysis of cellulose for oligosaccharide production in combined technology

Decomposition Behavior of Hemicellulose and Lignin in the Step-Change Flow Rate Liquid Hot Water

Kinetics of Lignocelluloses Hydrolysis in Supercritical Water

Analysis on Products of Saccharification of Lignocelluloses in Supercritical Water

The Experimental Research on Liquefaction of Lignocellulose in Sub-Critical and Supercritical Water

Analysis of Hydrolyzates Produced from Cellulose Catalyzed by Carbonaceous Solid Acid in an Ionic Liquid

Progress of Research of the Cellulose Saccharification in Supercritical Water

Highly Efficient Conversion of Sugarcane Bagasse Pretreated with Liquid Hot Water into Ethanol at High Solid Loading

Hydrolysis of Microcrystalline Cellulose to Produce Fermentable Monosaccharides by Plasma Acid

Investigation of cellulose supramolecular structure changes during conversion of waste paper in near-critical water on producing 5-hydroxymethyl furfural

The Preparation of Sugarcane Bagasse Microcrystaline Cellulose in Subcritical Water/Co2

Effect of Alcohol on Cellulose Hydrolysis in Super/subcritical Alcohol-Water Mixtures

Investigation of the Degradation Kinetic Parameters and Structure Changes of Microcrystalline Cellulose in Subcritical Water

Liquefied Production Distribution of Micro Crystallite Cellulose by Hydrothermal Decomposition