DISLOCATION FEATURES IN POLYSYNTHETICALLY TWINNED TiAl CRYSTALS AFTER DEFORMATION AT ROOM TEMPERATURE

Yi Liu,Donghui Lin,Dening Wang,Da Chen,) Nanjing,Zhiguo Liu

IF: 1.797

1996-01-01

ACTA METALLURGICA SINICA

Abstract:The dislocation features in polysynthetically twinned (PST) TiAl crystal deformed at room temperature have been investigated by TEM. Large amount of microtwins,1 / 2 110] ordinary dislocations, 011] and 1 / 2112] superlattice dislocations have been found. The 011] dislocations often dissociate according to the following mode:[101]→1 / 2[101] + APB + 1 / 6[211] + SISF+1 / 6[12] The 1 / 2 112] dislocations often dissociate to form faulted dipoles bounded by 1 / 6 1 12]partial dislocations. The effects of these features on the deformation of PST TiAl crystal at room temperature have been discussed.