The Microstructure of As-Melt Spun Al–7%Si–0.3%Mg Alloy and Its Variation in Continuous Heat Treatment

Mi Yan,Wuming Zhu,B. Cantor

DOI: https://doi.org/10.1016/s0921-5093(00)00791-7

2000-01-01

Abstract:The commercial A356 alloy was treated using melt spinning at rotating speeds of 20 and 40 m s−1, respectively. The as-melt spun ribbons were characterized by a combination of optical microscopy (OPM), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and X-ray diffraction (XRD). DSC tests were carried out to measure the microstructural evolution and melting of the ribbons during continuous heating, and microhardness of the ribbons under different conditions was also measured. It was found that at the chilling sides of A356 ribbons the matrix was composed of non-dendritic equiaxed grains, while at free sides the matrix was composed of dendritic grains. Silicon particles were found to preferentially precipitate along the grain boundaries on a nanometer scale at free sides. DSC tests indicated that in A356 ribbons the endothermic peaks of ternary Al–Mg2Si–Si eutectic melting drastically weakened, while the peaks of binary Al–Mg2Si eutectic melting vanished. The microhardness of the aluminum matrix at chilling sides of as-melt spun ribbons was significantly raised.