EFFECTS OF CONTENT OF FERROMAGNETIC PHASES ON PIT CORROSION BEHAVIOR OF AUSTENITE STAINLESS STEEL

Shao Guang-Jie,Yang Chao,Qin Xiu-Juan,Jing Qin,Riping Liu

2002-01-01

Abstract:In this paper the correlation between pit corrosive sensitivity of metastable austenite stainless steel (1Cr18Ni9Ti) with different deformation at lower temperature and the content of ferromagnetic phases is discussed. The test results show that this kind of stainless steel may induce α′-Martensite (ferromagnetic phase) and α′- Martensite when deformed at low temperature. Furthermore, the deformation-induced martensite has strong effect on its pit corrosive sensitivity when the ferromagnetic phase content is lower than 4.6%. The pit corrosive sensitivity increases with the ferromagnetic content. But when the content is within 4.6%~20.5%, it decreases with the content finally. When the content is higher than 20.5%, it increases again. This regularity can also be proved by electrochemical test and immersing test. Metastable austenite stainless steel is a kind of corrosion resistant metal material used widely in many fields. With appearance of a large number of defects, cold deformation can induce stainless steel to transform partly into martensite, which will decrease largely the corrosion resistance of the materials. Pit corrosion is generally a common corrosive form, which is a very harmful for the use of materials. It was regarded as a source of crack inducing stress corrosion fracture. Especially in the medium containing chloride, pit corrosion occurs very easily in metastable austenite stainless steel and can further induce stress corrosion fracture with the operation of stress, resulting in paroxysmal destruction and invalidation. Therefore, the study of correlation between pit corrosive sensitivity of metastable austenite stainless steel and its content of ferromagnetic phases plays an important role on controling corrosion resistance of stainless steel. 1. Experimental methods