EFFECT OF COLD WORKING ON PITTING SUSCEPTIBILITY OF 304 STAINLESS STEEL

胡钢,许淳淳,张新生,雒娅楠,王东

DOI: https://doi.org/10.3969/j.issn.1005-4537.2002.04.002

2009-01-01

Abstract:Cold working induced martensite content on type 304 stainless steel equipment was examined on-site.With different modes and different degree of cold working at room temperature,the martensite content was about 0.5%～10%.By potentiodynamic polarization,galvanostatic polarization and simulated occluded corrosion cell methods,the relationship between pitting potential(E b),pitting initiation potential(E np),corrosion potential(E corr) and martensite content on 304 stainless steel which had been prepared by low temperature(-70℃) tensile deformation was investigated in 3.5%NaCl solution.Experimental result showed that when the martensite content was between 0.1%(the material without low temperature tensile deformation) and 11.5%(the material with 10% low temperature tensile deformation),with the increasing of martensite content the potential of E b,E np and E corr changed negative(when then martensite content is 5%,the potentials were the most negative),the pH value in occluded cell dropped and the current density increased.It meant that cold working not only accelerated pitting initiation,but also accelerated pitting propagation of 304 stainless steel.